Abstract: Aluminum films were deposited on glass substrate by electron beam heat evaporation, and porous alumina films with high transmittance were prepared by means of anodic oxidation under different anodizing conditions in oxalic acid solution or phosphoric acid solution respectively. Thus the morphology of these porous alumina films was characterized by different structural. he optical transmittance spectrum at normal incidence over the 300~1000nm spectra region were obtained by spectrophotometer, which shows, in visible and ultraviolet light region, the transmittance of porous alumina films prepared in oxalic acid solution is much better than that prepared in phosphoric acid solution. The SEM analysis results showed that the pores are circular and uniform in porous alumina prepared in oxalic acid but irregular and non-uniform in that prepared in phosphoric acid, which affected the surface roughness of alumina films.

Abstract: Under the protection of argon gas, carbon nanotube reinforced magnesium metal matrix composite was made by stirring carbon nanotube into magnesium melts and formed by die casting. TEM and EDS methods were introduced to analyze boundary structure and chemical composition between carbon nanotube and magnesium metal matrix. The mechanical carbon nanotube properties of the composite were tested. Nickel chemical plating surface of carbon nanotube is favorable to adhesion of carbon nanotube to magnesium. Tests show that carbon nanotube, especially chemical nickel-plated one, has excellent role in strengthening the magnesium. The structure of magnesium was fined .The tensile strength, elongation, hardness and elastic modulus of the composite are improved.