Papers by Author: Yong Gang Deng

Abstract: One industrially C-Mn steel was studied in the present work. The Mn pre-partitioning process during continuous annealing was used. The results showed that the stability of retained austenite is increased because of the Mn pre-partitioning. The amount of retained austenite was about 5%, when increase the partition time to 100s. With the increase of the partition time, the amount of retained austenite increases, the tensile strength decreases, the yield strength and elongation both increase. Compared with quenching and tempering (Q&T) process, the tested steel after pre-partitioning quenching and partitioning (PQ&P) process has higher uniform elongation and the product of strength and elongation (UTS×TEL).

Abstract: The curves of true stress-strain of AZ80 Magnesium alloy had been tested with thermal simulation experiment, at the conditions of the experimental temperature being 260°C~ 410°C, and strain-rate being 0.001~ 10s-1, and the deformation degree being 50％. According the Arrhenius equation, a kind of constitutive equation of AZ80 Magnesium alloy which considered the strain had been put forward, and the relative errors between calculation results by the stress-strain model and experiment results are less than 10.5%.

Abstract: It had been studied that thermal deformation properties of super-alloy Inconel690(IN690) by thermal simulation on Gleeble 3800 Simulator, which the ranges of temperature was 1000～1200°Cand strain rates was 1.0～80/s. According to the experiment data, the critical conditions of super-alloy Inconel690 had been researched by strain hardening rate. Zener-Hollomn parameters (Z) had been introduced into establish the critical conditions of dynamic recrystallization, such as critical strain and critical stress and peak strain. The results showed that the critical strain model which established using strain hardening rate was in good agreement with that of Sellar’s model.