Abstract: Transparent indium-doped ZnO (IZO) films with low In content (<6at%) were fabricated through radio-frequency (rf) helicon magnetron sputtering. Formation of In-Zn-O solid solution was confirmed by X-ray diffraction (XRD) patterns. Incorporation of indium into ZnO films enhances the optical transmission in the visible wavelength. The optical band-gaps slightly increase from 3.25eV (ZnO) to 3.28eV (In0.04Zn0.96O) and to 3.30eV (In0.06Zn0.94O) due to Burstain-Moss effect. The Urbach tail parameter E0, which is believed to be a function of structural disorder, increases from 79meV (ZnO), to 146meV (In0.04Zn0.96O), and to 173meV (In0.06Zn0.94O), which is consistent with increase of Full-Width Half-Maximum (FWHM) in corresponding XRD patterns. Decreasing in crystal quality with increasing indium concentration is also confirmed by photoluminescence spectra.

Abstract: RF (Resorcinol-Formaldehyde) aerogels and carbon aerogels were prepared through the sol-gel method following the routes of polymerization, gelation, supercritical drying and pyrolysis processes. The influence of fabrication parameters on the textural structure of the samples, e.g., specific surface area, pore size, and pore size distribution, etc., were systematically investigated. With a decrease in the R/F molar ratio, or an increase in the catalyst content within a limited range, the porosity of the nanostructure materials increases. The optimal temperature of pyrolysis for RF aerogel was investigated by TGA (Thermogravimetric Analysis).