Abstract: The novel hemostatic film for the surgery of bone diseases was fabricated using TEMPO(2,2,6,6-tetramethylpiperidine-1-oxyl)-oxidized cellulose nanofibers (TOCNs), and phosphoryl oligosaccharides of calcium (POs-Ca) or sugar-containing hydroxyapatite (s-Ca₁₀(PO₄)₆(OH)₂; s-HAp). Three kinds of the hydrophilic and transparent films with the thicknesses of 10 to 20 μm were fabricated, i.e., TOCN, POs-Ca-added TOCN and s-HAp-added TOCN films. Among these films, the uptake amount of the simulated body fluid by s-HAp-added TOCN film was as high as 5,543%, which was expected to quickly stop bleeding of larger amount of blood for the hemostasis.

Abstract: The phosphoryl oligosaccharides of calcium (POC), extracted from potato starch, are composed of phosphorus oligosaccharides and calcium ions. Ultrafine calcium phosphate particles, whose main phase was hydroxyapatite (Ca10(PO4)6(OH)2: HAp), could be prepared through the hydrothermal treatment of POC solution at a temperature between 110 and 130°C; X-ray diffraction indicated the crystallinity of HAp in the resulting powder to be poor and similar to that of living bone. The present HAp powder was regarded to be calcium deficient carbonate apatite with the OH- group being partly substituted by a carbonate (CO3 2-) group. The solubility of the resulting powder in dilute hydrochloric acid was higher compared to that of commercially available HAp, suggesting excellent bioabsorbability for the present powder.