Abstract: Martensite morphology such as connectivity or dispersivity in ferrite (F)/martensite (M) dual-phase (DP) steels was investigated from topological viewpoint to reveal the effect of the martensite morphology on the mechanical properties. Topological analysis permits evaluation of the microstructural connectivity and dispersivity by measuring the number of handles, independent bodies and genus, etc. The topological analysis was performed on three-dimensional (3D) reconstructed images of the microstructure with different connectivity, dispersivity, volume fraction and hardness of martensite in DP steels that were prepared by changing the intercritical annealing temperature. The connectivity and the volume fraction of martensite increased while the dispersivity and hardness of it decreased with increasing annealing temperature. The effect of connectivity and dispersivity as well as volume fraction and hardness, in particular, on work hardening behavior was individually evaluated at a given strain.

Abstract: A 0.79C-1.5Si-1.98Mn-0.98Cr-0.24Mo-1.06Al-1.58Co (wt%) steel was isothermally heat treated at 200°C for 10 days to form a nano-scale bainitic microstructure consisting of nanobainitic ferrite laths with high dislocation density and retained austenite films. The crystallographic analysis using TEM and EBSD revealed that the bainitic ferrite laths are close to the Nishiyama-Wassermann orientation relationship with the parent austenite. There was only one type of packet identified in a given transformed austenite grain. Each packet consisted of two different blocks having variants with the same habit plane, but different crystallographic orientations. The presence of fine C-rich clusters and Fe-C carbides with a wide range of compositions in bainitic ferrite was revealed by Three-dimensional Atom Probe Tomography (APT). The high carbon content of bainitic ferrite compared to the para-equilibrium level of carbon in ferrite, absence of segregation of carbon to the austenite/bainitic ferrite interface and absence of partitioning of substitutional elements between the retained austenite and bainitic ferrite were also found using APT.