Papers by Author: Yu Wang

Abstract: The microstructure evolution of TiAl intermetallics with different microstructures loaded under different strain rates and temperatures was investigated. The results showed that the deformation twinning dominated the deformation process under high strain rate, while dislocation slip was another dominating deformation mode under quasi-static loadings. The proportion of twinned grain increased with the increased strain rate. In Duplex TiAl, the plastic deformation was mainly found in equaxied grains and seldom found in lamellar grains.

Abstract: The microstructure evolution of Ti-46.5Al-2Nb-2Cr with different microstructure types loaded under a large range of strain rates and elevated temperatures is investigated by TEM. The results show that deformation twins are the main deformation mode under high strain rate loadings and both ordinary dislocation and super-dislocation are the additional modes under quasi-static loadings. The proportion of twinned grains increases with the increased strain rates.

Abstract: The effect of temperature and strain rate on the mechanical behavior and microstructure evolution of Near Gamma Ti-46.5Al-2Nb-2Cr (NG TiAl) was investigated at temperatures ranging from room temperatures to 840 under strain rates of 0.001, 320, 800 and 1350s-1. The TEM analysis indicated that deformation twinning and stacking fault are the main deformation modes under dynamic loadings and dislocation slip is another important deformation mode under quasi-static loadings. The density of deformation twinning and/or stacking fault increases with the increased temperature and strain rate.