Papers by Author: Yuan Fu Yi

Abstract: Objective: To study the relative translucency of 4 veneered and glazed all-ceramic systems core material, including Vita In-Ceram Alumina, Vita In-Ceram Zirconium, Ivoclar Vivodent Empress and Colored Zirconia. Methods: Under standard black and write background, the surface light reflectivity of 4 veneered all-ceramic systems core material was determined with contact color difference meter, and the ratio of Yb /Yw was calculated. Results: After veneered, the relative translucency of 4 core materials all declined, and ranged from 0.8015 of Colored Zirconia to 1.00 of In-Ceram zirconia, among of that Empress II and Colored Zirconia were most transparent. Conclusion: Among the groups, there is no significant difference between Empress II and Colored Zirconia(IL1,IL2,IL3). Compared with Vita In-Ceram Alumina and Vita In-Ceram Zirconium, Vita In-Ceram Alumina(AL1) has significant difference. There is no significant difference between Vita In-Ceram Zirconium and Vita In-Ceram Alumina(AL2,AL3,AL4).

Abstract: Objective: We aimed to develop a multi-functional CCS/CCM (Computerized Color Selecting/Computer Color Matching) software so as to provide more practical colorimetric software for clinical use and further researches. Methods: This software used the 6 dental prosthetic materials and color data from 4 shade guide system which were most frequently-used in clinic currently as basic database, to program 5 functional blocks including respectively CCS/CCM system; Dental Material Chromatic Value System; Vita Information System; Transformation of Colorimeter System; and Chromatic Value Difference Analysis. These modules had the functions of information inquiry of different types of dental materials and their corresponding chromatic value, color matching, transforming, and color difference analysis. Results: The software had a convenient operation interface which could guarantee a stable performance. Containing various shade block and chromatic value, and transformation among different colors, this software analysed the color difference in the database, improved the accuracy and reliability of dental color choosing, and, to some extent, increased the color repetition rate of prosthesis. Conclusion: The software could well meet the needs of clinical dental colorimeter and choosing, increase the color repetition rate of prosthesis, and easily finish the transformation among different colors. It had more functions to adapt clinical need.

Abstract: The purpose of this study was to compare the transmittance of four dental all-ceramic core materials at clinical recommendation thickness.Specimens with 10mm in diameter and 0.50.01mm in thickness,including IPS e.max Press,Zenostar Zirconia,Lava Zirconia and Upcera Zirconia,were fabricated.The transmittance of specimens were measured with PR2650 spectrophotometer and measurements were analysed statistically with SPSS13.0.Experimental results showed that they had significantly different transmittance.There was a decreasing order,IPS e.max Press Lava Zirconia Zenostar Zirconia Upcera Zirconia,which were 6.1136.750 for IPS e.max,1.6042.135 for Lava Zirconia,1.5782.117 for Zenostar Zirconia and 0.9951.265 for Upcera Zirconia.

Abstract: The need for bone repair has increased as the population ages. However, currently, the bone grafts still have some disadvantages, such as low compressive strength and porosity, which limit their use. In order to solve these disadvantages, in this study, the porous beta-tricalcium phosphate (β-TCP) anorganic bone graft were prepared from healthy bovine cancellous bone by cell-free, defat and twice calcinations. X-ray diffraction (XRD) was used to investigate the chemical composition of the bone graft. And the morphology, porosity and mechanical strength of the bone graft were also evaluated. The results showed that most constituent of the bone graft was β-TCP. In addition, the bone graft scaffold exhibited the macro and micro porous structure and the porosity was 57.63%, just as the nature cancellous bone. The compressive strength was 4.47±0.63MPa. Above all, the porous β-TCP anorganic bone graft not only has similar chemical composites as the nature cancellous bone, but also it can effectively retain the porous structure of natural cancellous bone and provides optimal channels for the ingrowth of new bone and blood vessels.Therefore, the porous β-TCP anorganic bone graft is a potential biomaterial in bone tissue engineering.

Abstract: Aim To explore pigmented glass for infiltration and investigate its physical and mechanical properties. Methods The pigmented glass was prepared by melting glass components in an alumina crucible at 1400°C for 2h. The thermal properties were tested using a Setaram-TGDTA 92 analyzer; three point bending strength and fracture toughness were also tested; the microstructure of the glass was studied using a scanning electron microscope. Results The thermal expansion coefficient over the range 20–600 °C was 6.2 × 10-6 °C -1, Tg was about 690 °C, the density, bending strength, fracture toughness and Vickers hardness were 2.23 g/cm3, 118 MPa, 1.22 MPam1/2, and 7.4 GPa respectively. Conclusion The pigments have no detrimental effects on the physical and mechanical properties; thus the pigmented glass for infiltration has favorable physical and mechanical properties and also good compatibility with presintered porous alumina.

Abstract: The purpose of this study was to study effects of the mechanical properties of veneering porcelain on stress distribution of dental zirconia layered structure by three-dimensional finite element analysis. A 3-D geometric model of the first maxillary molar was established, a tooth preparation was simulated by the Imageware software. A crown was designed and divided into three layers: core, middle layer and outer veneer layer. The elasticity modulus of the middle layer was 70GPa for the control model up to 175GPa for the tested models. Loads of 200N were applied over a 1 mm diameter area beneath the tip of the mesial-distal cusp, simulating typical occlusal contact areas, the stress distribution of the crown systems were analyzed. Results show that within the geometry of the crown configuration, one concentration district of maximum principal stress occurred on the occlusal surface closely proximal to the loading position, several sub-maximum principal stress area were observed, such as margin regions of the mesial face, lingual face, distal faces, buccal face and occlusal fossa. Middle layer with higher modulus can effectively disperse the stress concentration in the layered zirconia all-ceramic crown system.

Abstract: Low temperature aging (LTD) is an important factor of Y-TZP ceramic as artificial joint femoral head and dental restorative materials in vivo for long-term application. In this paper, the accelerated aging experiments on Y-TZP ceramics were conducted. The t-m phase transition is occurring from the surface to the inside during low temperature aging of Y-TZP ceramics. As content of phase transformation increases, thickness of phase transformation layer increases. While the content of surface monoclinic phase is less, the volume expansion and surface stress caused by phase transformation can make cracks and holes shrink or even close, then the flexural strength increase. As a large number of surface monoclinic phase was generated, due to there are a lot of microscopic defects in the phase transition layer, crystals loose, strength of grain boundary lower than that of not aging area and phase transformation layers fracture in the intergranular mode, that damages the flexural strength. Therefore, the flexural strength increase firstly and then decrease with the increase of surface monoclinic content.

Abstract: The matching properties of ceramics and veneering porcelain play an important role for the overall color and mechanical properties of dental crowns. The Vita VM9 veneering porcelain was coated on the surfaces of two zirconia, three-point flexural strength, heat shock resistance and the overall color after veneered with porcelain were tested. The results showed that the interlayer cracks, radial cracks or porcelain body cracks were not appeared in all samples during thermal shock experiments at 60~220°C. Their flexural strength was all above 700MPa and the overall color covered the common color of VITA-3D Master shade guide. There is good thermal compatibility between the two dental shaded zirconia ceramics and Vita VM9 veneering porcelain. The mechanical properties are suitable for clinical posterior teeth area restorative, and the overall color is also suitable for the requirements on the color and brightness of clinical dental restoration.

Abstract: To evaluate the masking ability of IPS e.max all-ceramics system of HO series. IPS e.max Press HO ingots were fabricated into twenty cylindrical specimens (n=5) with the diameter of 13mm and four different thinknesses (0.4mm, 0.6mm, 0.8mm, 1.0mm). All specimens after veneered, gazed and cemented to metal substrate disks (thickness 3mm, diameter 13mm) were measured on both the white background and metal substrate disks background using a spectrophotometer and values of L, a and b were calculated to compare color differences among four groups. Meanwhile ΔE with the preselected required color (A2 color) were calculated. ΔE<1.5 was considered a clinically acceptable color match. In the 0.4mm thickness specimens group, the values of L, a and b significantly increased (-1.36±0.05, -0.15±0.06, -1.46±0.02, respectively) between the white background and abutment background. But there were no significant color differences in the other three groups (P<0.05). In the 0.6mm and 0.8mm thicknesses specimens groups, the color difference values (0.71±0.04, 1.14±0.06, respectively) with A2 color were less than the defined value. Thus the cylindrical specimens with the thickness of 0.6mm, 0.8mm and 1.0mm could mask the metal substrate disks background sufficiently and the thickness of 0.6mm and 0.8mm had an acceptable color match compared with the target color. IPS e.max all-ceramics system of HO series can produce clinically acceptable color match and have the capacity to mask a dark background such as a dark tooth or core buildup material.

Abstract: Despite the expanded application for zirconia in restoration dentistry, there is less clear recommendation in the literature regarding the relation between zirconia surface roughness and its shear bond strength to resin cements. The aim of this study was to assess the effect of surface roughness of Cercon zirconia on its shear bond strength to resin cements. 66 Zirconia rectangular specimens (10 mm×10 mm×3 mm) were prepared from Cercon zirconia blocks, finished using a diamond rotary cutting instrument, sintered, and then assigned into 6 groups. The specimens in the first group without polishing were used as control. Other groups were polished against 120#, 240#, 360#, 500# and 600# sand paper after sintered, respectively. Ceramic surface were analyzed by scanning electron microscopy (SEM) and Surface profilometer. 10 samples of each group were bonded with Variolink N resin cements respectively and submitted to shear bond strength test. Shear bond strength was measured and statistically analyzed. The results showed that the population means of 6 groups of samples were not equal. There was no significant difference between control group and 600# sand paper treated group, 500#, 360# and 240# sand paper treated groups (P>0.05), but a significant difference among the other groups (P<0.05). Findings of this study revealed that the shear bond strength might be raised by increasing the surface roughness of Cercon zirconia. Therefore, the surface roughness of Cercon zirconia has an effect on the shear bond strength, but is not the determining factor in clinical use.