Papers by Author: Yuan Zhan

Abstract: This paper reports the investigation on both high and normal strength concrete using a non-contact electrical resistivity facility. The bulk resistivity development (ρ(t)-t curves) of the fresh concretes was evaluated from casting to 72h. The relationship between the electrical resistivity and the pore structure obtained from mercury intrusion porosimetry (MIP) method was analyzed. And the compressive strength evolution of fresh high- and normal- strength concrete was studied based on the bulk resistivity at early ages. The experiment results indicated a linear relationship between the fractional porosity and electrical resistivity. A further correlation between the compressive strength and electrical resistivity was analyzed with Archie’s law. Based on these studies, it appears that the electrical resistivity test could provide information for the design, quality control, quality assurance, and utilization of both high- and normal- strength concrete.

Abstract: Reaches on durability of concrete has been made great advances over the past decades. However, little works have been done on the corrosion of reinforced concrete exposed to boric acid in cooling pond of heating exchange system of nuclear power plant. The purpose of this study is to experimentally investigate the behavior of reinforced concrete in such circumstance. Tests were carried out on specimens cured in a standard moisture room at a temperature of 20±3°C. Three different concentration of boric solution (2000ppm, 8000ppm, 30000ppm) were simulated to accelerate the corrosion. The compressive and splitting tensile strength,elastic modulus of concrete , mass loss rate of steel bar, bond strength and flexural bearing capacity of reinforced concrete at 60, 90, 120, 150 and 180 days were obtained respectively. The results indicate that the presence of boric acid below 30000ppm does not significantly affect serviceability of concrete. The corrosion is slight for the specimens with crack less than 0.4 mm under flexural loads. Boric acid almost has no effect on the corrosion of the steel bar and bond strength.