Papers by Author: Yuki Mizutani

Abstract: Thin films of MBi₄Ti₄O₁₅ (M = Ca and Sr) with preferential crystal orientation were fabricated using underneath perovskite layers on various substrates. One-axis BLSD films on (100)LaNiO₃/(111)Pt/Ti/(100)Si and epitaxial BLSD films on (100)SrRuO₃//(100)SrTiO₃ were fabricated by chemical solution deposition (CSD). Dielectric constants of the CaBi₄Ti₄O₁₅ and SrBi₄Ti₄O₁₅ films on (100)LaNiO₃/(111)Pt/Ti/(100)Si were approximately 250, while those on (100)SrRuO₃//(100)SrTiO₃ were 220, respectively. The temperature coefficients of capacitance (TCCs) of these films were below 10% in atmospheric temperature range between R.T. and 300°C, which is significantly smaller than those of conventional (Ba,Sr)TiO₃-based capacitors.

Abstract: Thin films of a bismuth layer-structured dielectric oxides (BLSD), SrBi4Ti4O15, with preferential crystal orientation were prepared by means of chemical solution deposition (CSD) technique on (111)Pt/(100)Si substrate with bottom nucleation layers of conductive perovskite oxides, LaNiO3 and SrRuO3. CSD technique was utilized for the film preparation of SrBi4Ti4O15. These films possessed highly crystal orientation of (00l) BLSD planes parallel to the substrate surface. The leakage current densities of the SrBi4Ti4O15 films on (100)SrRuO3//(100)LaNiO3/(111)Pt/Ti/(100)Si and on (100)LaNiO3/(111)Pt/Ti/(100)Si were approximately 10-6 and 10-7 A/cm2 respectively. The dielectric constants of these films in a frequency range of 102 - 106 Hz were from 310 to 350 and 250 to 260 respectively. The value of capacitance change of these films in the range from 20 to 300 oC was about +8 and +5% respectively.