Papers by Author: Zhen Liu

Abstract: There were different heat treatments to Cu-Zn-Al shape memory alloy. Cement-based smart lost-circulation control material was prepared by the method of rolling agglomeration. And indoor simulation experiment was carried out. The results show that the heat treatment temperature is 800°C, the quenching medium is the boiling water; the leakage is decreased with the increase of the cotton fiber content. When the cotton fiber content is 4%, the leakage is the minimum; the best volume percent of the lost-circulation control material is 20% in the grout.

Abstract: With an average diameter of 148-285 nm and a conductivity of 2.38E^-2- 5.88 E^-2S/cm, Nanoscaled polyaniline (PANI) were synthesized based on template-free method in the presence of dicarboxylic acids dopants (e.g., D-tartaric acid, Succinic acid, maleic acid and fumaric acid). Furthermore, the trans-cis isomerization of butenedioic acid plays an important role in the formation of nanostructures from plane-like to nanofibers, and PANI-MA has larger diameter, higher crystallinity and conductivity than PANI-FA.

Abstract: Different heat-treatments were carried out on the Ti-Ni shape memory alloy, alloy thread was made to straight line with the self-made alignment on 500 °C and then self-made angle training meter was used to train the alloys. Cement-based smart materials were prepared by the method of rolling agglomeration. Finally, indoor simulation experiment was carried out. The results show that the shape recovery ration becomes lower when quenching medium are hot-oil, hot-water, cold-oil and cold-water. The smart lost-circulation control material response quickly to external environment, the time from contact with external environment to the begin of distortion is less than or equal to five seconds, and to the end of distortion is less than or equal to sixty seconds.The best volume fraction for cement-based smart plugging material in cement slurry is 20%. Furthermore, the lost-circulation control material possesses the characteristics of a short time plugging and a strong pressure-bearing capability after plugging. And it improves the capacity of the ordinary cement-based smart lost-circulation control material.

Abstract: Porous materials were prepared by sintering using C as place holder and SiO2 as based, mixed with paraffin. Then Organic-inorganic Core-shell Particles were made by crushed. With the help of XRD and SEM, on the 60°C Study on Sulfate-Corrosion Resistance of cement Mixed with Organic-inorganic Core-shell of Preparation. The Organic-inorganic Core-shell Particles made by accounted of C 15% and heat preservation 4h in 920°C were the best. The results showed that when the content of Organic-inorganic Core-shell Particles was 15%, the Sulfate-Corrosion Resistance reached the climax.