Papers by Author: Zhong Bo Hu

Abstract: A new series of solid solutions Dy2-xGdxMo4O15 (x = 0.0-0.9) were prepared. These compounds all crystallize in monoclinic structure with space group P21/c. The lattice parameters a, b, c and unit cell volumes V increase almost linearly with increasing gadolinium content. The intrinsic thermal expansion coefficients of Dy2-xGdxMo4O15 (x = 0.0 and 0.25) were obtained in the temperature range of 25 to 500°C with high-temperature X-ray diffraction. The correlation between thermal expansion and crystal structure was discussed.

Abstract: Compounds Yb2Mo3O12 and Lu2Mo3O12 were prepared by conventional solid-state reaction. Their crystal structures and thermal expansion properties were investigated. It was found that Yb2Mo3O12 and Lu2Mo3O12 adopt orthorhombic structure and show negative thermal expansion (NTE) in the temperature range of 200-800 °C. Their a-axis and c-axis exhibit stronger contraction in the temperature range of 200-800 °C, while b-axis slightly expands in the temperature range of 200-300 °C and then contracts in the temperature range of 300-800 °C. The linear thermal expansion coefficients al of Yb2Mo3O12 and Lu2Mo3O12 are −5.17 × 10−6 °C−1 and −5.67 × 10−6 °C−1, respectively.

Abstract: A new systematic study of the formation and structure of solid solutions Gd (5-x)HoxSi4 (x = 1.0-5.0) has been performed. By X-ray powder diffraction method, it was found that these compounds all crystallize in orthorhombic structure with space group Pnma and the cell parameters a, b, c and the volume of unit cell are correlated with the holmium content.

Abstract: The spark plasma sintering technique was used to fabricate ceramics from Pb(Mg1/3Nb2/3)O3– PbTiO3 ceramic layers which were prepared by tape casting and TGG method used BaTiO3 templates as seeds. During heat treatment, epitaxial grain growth occurred on the BaTiO3 surfaces and formed <001> textured lead magnesium niobate-lead titanate, Pb(Mg1/3Nb2/3)O3-0.325PbTiO3 (PMN-32.5PT) ceramics. The phase compositions and microstructure were investigated. The results indicated that this method was an alternative sintering technology to synthesize dense lead-based relaxor ferroelectric ceramics.