Abstract: Barium-bearing glass samples were fabricated using raw material from the beneficiation of local resource. Nd₂O₃ was added in various concentrations. Dielectric constant, density, refractive index, and absorption spectra of the glass samples were measured. It was found that the densities and refractive indices increased with increasing Nd₂O₃ contents. The dielectric constant and absorption spectra were plotted and discussed.

Abstract: Lead glass that shows a high refractive index is the best known and most popular for radiation shielding glass. Due to the toxic of lead compounds on the human organisms as well as the environmental issues, lead free glass was fabricated by using some heavy elements such as barium and bismuth to replace lead. In this study, colorless lead free glass samples were prepared from 40 wt% local quartz sand and various concentration of BaCO3 (20-40 wt%) as the main compositions in order to study radiation shielding property. The glass mixtures were melted conventionally using electric furnace at the maximum temperature of 1250°C with 4 hr dwelling time. The gamma attenuation characteristics were studied for the photon energy of 662 keV from Cs-137. Density and refractive index were also determined. It was found that a variation of prepared glass samples can be produced both in terms of clarity and radiation shielding properties. The attenuation coefficients were linearly increased as the increase of BaCO3 content. The density and refractive index were also increased. The linear and mass attenuation coefficients of the glass sample containing 40 wt% BaCO3 were 0.234 cm-1 and 0.0726 cm2g-1. In conclusion, a low density glass samples will give rise less attenuation than a high density ones. It can be concluded that the lead-free high refractive index glass that is one of the environmental materials can be used as the gamma radiation shielding glass.

Abstract: Barium-bearing glass samples were fabricated in a laboratory scale using quartz sands that was a by-product of feldspar floatation in Tak Province, northern Thailand, and 30-wt% barite from Loei Province, northeastern Thailand, as the main compositions. Cr2O3 of concentrations ranging from 0.01 to 5.0 wt% was doped into the glass mixture. The dried powders were wellmixed in a ceramic crucible and melted in an electric furnace at 1250°C for 6 hr. Bubble-free glass samples were yielded after cooling down. The glass colors were changed from colorless to green by the addition of Cr2O3. Dielectric property, color, specific gravity, and refractive index of the glass samples were analyzed. It was found that dielectric constant, specific gravity, and refractive index increased with increasing amount of Cr2O3 dopant. Measurements of UV-VIS-NIR spectra and microstuctural analysis using scanning electron microscope were also carried out and discussed.