Papers by Keyword: Continuous Dynamic Recrystallization CDRX

Abstract: The hot rolled AA6082 aluminium alloy with aluminide dispersoids is deformed up to large strains to obtain a fine grained microstructure. Friction stir spot welding (FSSW) is carried out on rolled plates by means of a device provided by MTS System Corporation. FEM simulations determine that the material can flow up to local strains between 10 and 50 when the material reaches temperatures between 300-500°C. With this information, hot torsion tests at constant temperatures are carried out in a Gleeble ® 3800 machine for different strain rates. In both cases, in situ water quenching is applied to freeze the microstructure and avoid any static recrystallization effect after hot deformation. Light optical microscopy is used to identify the evolution of the grains as a function of the local deformation parameters determined by FEM simulations. The microstructure development by FSSW as well as by torsion is then further characterized by means of EBSD. At small strains the material deforms mainly by dynamic recovery with small low angle grain boundary formation and boundary dragging by fine aluminides and Mg2Si. At large strains grain refinement by continuous dynamic recrystallization takes place heterogeneously as a function of the original crystallographic orientation and precipitation state of each grain.

Abstract: The high temperature deformation behavior of AISI 430 ferritic stainless steel has been studied over a temperature range of 800 to 1000°C and strain rate of 0.05-5.0/sec. The evolution of flow stress and microstructures showed the characteristics of continuous dynamic recrystallization (CDRX). The flow stress curves gradually decreased with increasing strain over the peak stress until 500% of strain without any steady state shown in typical austenitic stainless steel. Sub-grains of low angle firstly formed along the original high angle grain boundary were propagated into the inside of original grain and transformed to high angle. The CDRX grain sizes of AISI 430 deformed at 1000 °C and 0.5/sec was about 30-35㎛.