Papers by Keyword: Cork Agglomerate

Abstract: Aerospace components are characterized by having high strength to weight ratios in order to obtain lightweight structures. Recently, different types of sandwich components using composite materials have been developed with the purpose of combining the effect of reinforced face-sheets with low weight core materials, such as honeycombs and foams. However, these materials must combine damage tolerance characteristics with high resistance under both static and dynamic loads. Cork composites can be considered as an alternative material for sandwich components since cork is a natural material with some remarkable properties, such as high damage tolerance to impact loads, good thermal and acoustic insulation capacities and excellent damping characteristics for the suppression of vibrations. The experiments carried out in this investigation were oriented in order to optimize the specific strength of cork based composites for sandwich components. Static bending tests were performed in order to characterize the mechanical strength of different types of cork agglomerates which were obtained considering distinct production variables. The ability to withstand dynamic loads was also evaluated from a set of impact tests using carbon-cork sandwich specimens. The results from experimental tests showed that cork agglomerates performance depends on the cork granulate size, the type of reinforcing elements and the bonding procedure used for the cohesion with the matrix material.

Abstract: The environment is a prominent issue today. Designing environmentally sustainable products is an attempt to address this question. In many cases, natural materials are environmentally friendly for product design manufacturing. The goal of this work is to study the mechanical behaviour of NL10 and NL30 cork agglomerates. Compression, shear and bending tests in sandwich specimens made of glass or jute fiber in facings and cork agglomerates as core were carried out. The sandwich specimens were manufactured by Resin Transfer Moulding (RTM) process. Results show that NL30 has a higher compression strength and shear resistance than NL10 agglomerate due to its manufacturing process, which originates superior density, but the NL30 agglomerate superior density is undesirable. Sandwich test specimens that presented failure by rupture of the core in both types of tests, core shear tests and three point bending tests, showed that the failure is mainly adhesive occurring between the adhesively joined cork grains. Since grains are unaffected and remain intact, it is possible to improve these materials by using better agglutinants and new bonding techniques with the intent of getting cork agglomerates with higher shear and flexural strength.