Abstract: The Cu thin films were prepared at room temperature by radio frequency magnetron sputtering on p-type Si (111) substrates. The surface morphology and interface reaction of Cu thin films were studied at different deposition condition by scanning electron microscopy (SEM) and X-ray diffraction (XRD). The results show that the existence of the native silicon oxide layer suppresses the interdiffusion and interface reaction of Cu and Si. The formation of the copper-silicide phase is observed by XRD when the annealing temperature arrives at 450 °C.

Abstract: The Cu thin films were deposited on P type Si (111) substrates by ionized cluster beam (ICB) technique. The surface morphology and roughness of Cu thin films were studied at different deposition condition by atomic force microscopy (AFM). The results show that the average grain size and surface roughness of the Cu thin films deposited at an acceleration voltage of 3 kV is smaller than other conditions.

Abstract: For optimum fabrication and usage of Cu films, an understanding of the relationship between processing and microstructure is required. The existence of twins is another significant factor for texture development in Cu films. Texture character and strength in the Cu film is dependent on the twin boundary development that is a function of processing conditions and film thickness. In this study, determination of grain growth and texture in the sputtered and electroplated Cu films during annealing was performed for films of 100, 480 and 850 nm in thickness deposited on a Ta(25 nm)/Si wafer. The texture was measured by X-ray pole figure. The effect of film thickness on the annealing texture in the sputtered and electroplated Cu films is examined and discussed.