Papers by Keyword: Deformed Microstructure

Abstract: In this paper, a new type steel plate with nano-layered martensite lath structure was produced by heavy cold-rolling. After rolling, subsequent annealing has great effect on the deformed martensite morphology and grain refinement. Microstructure recrystallizing course have occurred after long time annealing at 350°C. The recrystallization activation energy is 151 kJmol-1. The ultrafine ferrite grains (average grain size about 317nm), nano-carbides precipitated uniformly were seen in the specimen annealed at 500 °C. Annealing at and above 600 °C resulted in coarse ferrite grains with spheroidized coarse carbides, causing grain growth.

Abstract: The uniformity of grain coarsening throughout the microstructure of a submicron grained particle-containing aluminium alloy has been investigated using high resolution EBSD. The alloy was processed by equal channel angular pressing (ECAP) and low temperature ageing to generate ~0.8 􀁐m diameter grain structure containing a relatively uniform dispersion of nanosized Al3Sc particles. While the initial processing route generated a uniform grain size distribution, the distribution of grain orientations was rather inhomogeneous with certain regions of microstructure containing colonies of grains consisting predominantly of either HAGBs or LAGBs. It was found that, despite the difference in grain boundary character between these regions, the fine particles produced by pre-ageing promote uniform coarsening throughout the microstructure despite the marked differences in boundary character between these regions. An analytical model is outlined which predicts the uniformity of grain coarsening in particle-containing alloys despite the presence of orientation gradients in the microstructure.