Papers by Keyword: Electrochemical Noise Analysis

Abstract: It is believed that the dissolution of chalcopyrite (CuFeS2) in acid medium can be accelerated by the addition of Cl- ions, which modify the electrochemical reactions in the leaching system. Electrochemical noise analysis (ENA) was utilized to evaluate the effect of the Cl- ions and Acidithiobacillus ferrooxidans on the oxidative dissolution of a CPE-chalcopyrite (carbon paste electrode modified with chalcopyrite) in acid medium. The emphasis was on the analysis of the admittance plots (Ac) calculated by ENA. In general, a stable passive behavior was observed, mainly during the initial stages of CPE-chalcopyrite immersion, characterized by a low passive current and a low dispersion of the Ac plots, mainly after bacteria addition. This can be explained by the adhesion of bacterial cells on the CPE-chalcopyrite surface acting as a physical barrier. The greater dispersions in the Ac plots occurred immediately after the Cl- ions addition, in the absence of bacteria characterizing an active-state. In the presence of bacteria the addition of Cl- ions only produced some effect after some time due to the barrier effect caused by bacteria adhesion.

Abstract: The electrochemical response of chalcopyrite was studied using electrochemical noise analysis (ENA). The assay was carried out under constant aeration using 30 mL in two electrochemical cells containing iron-free mineral salts solution. These cells were initially monitored for 56 hours. After 72 hours, 7.25×1010 cells mL-1 of A. ferrooxidans strain LR were added in both cells and monitored until 128 h. Subsequent to this period, 0.927 mmol L-1 of silver ions and 400 mmol L-1 of chloride ions were added each one separately. Both conditions were monitored until 168 hours. According to results obtained, it was observed that Cl- ions addition induced an accelerated corrosion process. However, there is a tendency of the system to reach the stationary state due to repassivation of the electrodic surface. In the other side, the Ag+ addition contributed for the maintenance of the oxidant atmosphere, in spite of controversial effect caused by considerable variations in the Rn values, resulting in a instability in the chalcopyrite reactivity.