Abstract: High levels of surface shear experienced during rolling, grinding or machining can cause 6000 series aluminium to develop an ultra-fine grained surface layers which dramatically increase susceptibility to filiform corrosion (FFC) under paint films. In-situ Scanning Kelvin Probe (SKP) measurements in humid air are used to compare the kinetics and mechanism of FFC on abraded and lacquer-coated samples of high copper containing AA6111 and low level copper AA6016. FFC is initiated by applying a small volume of aqueous HCl to a penetrative defect on polyvinylbutyral (PVB) coated alloy samples prior to placement in a chamber maintained at constant humidity and temperature. The SKP is then repeatedly scanned over a fixed surface area to produce a time-lapse animation showing the dynamic evolution of localized free corrosion potential patterns. The spatial distribution of potential variation provides insight into the FFC mechanism and the numerical integration of areas of dissimilar potential provides a measure of the time-dependent area of coating delamination. Various possible FFC inhibition strategies are investigated for use under circumstances where removal of the surface layer prior to application of an organic (paint) coating is not feasible. The two strategies shown in this paper are the use of an anti-corrosion pigments based on an intrinsically conducting polymer called polyaniline. An anion-exchange pigment called hydrotalcite is also used.

Abstract: Scanning Kelvin Probe (SKP) potentiometry is used to systematically investigate the effect of surface abrasion and subsequent heat-treatment on the open-circuit potential in humid air of the AA6016 surface. SKP is also used to follow the kinetics of filiform corrosion and to determine characteristic potentials associated with the electrolyte-filled filiform head and dry filiform tail. It is shown that simply abrading with 180 grit SiC produces a surface potential up to 0.5V lower than the bulk. When the abraded sample is overcoated with a 30 micron layer of PVB (polyvinyl butyral) and exposed to HCl a fast, superficial filiform corrosion (FFC) is observed in which metal loss is limited to the thickness of the surface layer. Filiform head OCP values are similar to that of the surface layer, whereas filiform tail OCP values are similar to the bulk. A mechanism is proposed in which the ultra-fine grain structure of the surface layer produces an anodic activation and the potential difference between the surface layer and the bulk provides and increased thermodynamic driving force for corrosion. For post-abrasion heat treatment temperatures up to 350°C the fast filiform process is followed by a slower, deeper form of FFC.