Papers by Keyword: Gahnite

Abstract: Mullite-gahnite composites with different phase-proportions were prepared using sol-gel process. Crystallization path was determined using differential thermal analysis (DTA). X-ray powder diffraction (XRD) was used to study the crystal phases development. The course of the thermal reactions is dominated by the intermediate formation of two spinel phases. The former phase was attributed to gahnite, while the latter to Al-Si spinel. Zn loading decreases amounts of mullite and α-alumina, while increases gahnite and amorphous phase. The observed microstructure of sintered bodies is characterized by fine gahnite particles distributed among larger mullite grains, which is highly favourable for ceramics with high mechanical requirements.

Abstract: The crystallisation mechanism of glass-ceramic materials from a CMAS group Al0.37B0.34Fe0.01Mg0.02Zn0.29Ca0.05Si0.78O3 was tested under non-isothermal conditions by the DTA method. Glass-ceramic material of two-phase composition with precipitation of crystallites from islet silicates Zn2SiO4 and a crystalline phase from a spinel group, gahnite ZnAl2O4 was obtained in the system under investigation. Activation energy of a crystallization process Ea was determined and a crystal growth morphology parameter n was computed. It was revealed that in the test material from a CMAS group one could obtain the crystalline phase in the form of ghanite as a result of a controlled process of crystallization. The occurrence of a spinel phase caused the obtained glass-ceramic material had higher fracture toughness (KIC) than material from a CMAS group, containing pyroxene crystalline phases typical for this system.