Papers by Keyword: High-Pressure Sliding

Abstract: Grain refinement is an important prerequisite for advent of superplasticity. In particular, as the grain size is smaller, the superplasticity appears at higher strain rates and lower temperatures. Severe plastic deformation (SPD) is a useful process for achieving significant grain refinement. This presentation shows that applicability of the SPD process is enhanced when it is operated under high pressure through high-pressure torsion (HPT) and high-pressure sliding (HPS). It is demonstrated that commercially available conventional alloys but less ductile alloys such as Mg alloys, age-hardenable high-strength Al alloys (A2024, A7075) and Ti alloys become superplastic after processing by HPT or HPS.

Abstract: An earlier study showed that high-pressure sliding (HPS) is effective for grain refinement of pure Al in a rectangular sheet form using the principle of high-pressure torsion. In this study, the HPS is applied for grain refinement of an Al-3%Mg-0.2%Sc alloy and an AZ61 Mg alloy. HPS was conducted under a pressure of 1 GPa with sliding distances of 10 to 30 mm at room temperature for the Al alloy and at 473 K for the Mg alloy The average grain size is ~300 nm for both the Al and Mg alloys, respectively. Tensile tests showed that a superplastic elongation of ~1500% is achieved in the Al-3%Mg-0.2%Sc alloy at 573 K with an initial strain rate of 3.3x10-3 s-1 and of ~600% in the AZ61 alloy at 573 K with an initial strain rate of 1x10-3 s-1.