Papers by Keyword: High Resolution Transmission Electron Microscope

Abstract: The age hardening precipitates of Mg-4.7mass%Zn alloy aged at 423K,473K were studied by using high-resolution transmission electron microscope (HRTEM). Contrasts of mono layers were confirmed to exist on the (0001) and (1100) matrix planes. It was considered that the contrast of mono layer was plate-like shape, and identified as pre-precipitates from as-quenched stage to early stage of aging at 473K for 32h . In the peak aged specimen of aged at 473K, the β1’ phase was observed. The β1’ phase has a rod-like shape and parallel to c-axis of Mg matrix. It can be observed orientation relationship between Mg matrix and β1’phase has not only same parts to previous reports but also different parts in one β1’ phase .

Abstract: High resolution transmission electron microscopy（HRTEM）observation was performed to clarify morphology of precipitates at early stage of aging in Mg-Gd-Zr alloy. In the specimen aged at 423K, monolayer was observed on {1100}Mg planes. With increasing aging time, the monolayer and β” phase grew along the <1120>Mg directions. Arrangement of bright dots corresponding to {020}β’ except for the monolayer and β” phase was observed before peak aging stage. β’ phases formed at the same aging stage. Thus, these precipitates co-existed before peak aging stage. The monolayer, β” phase and β’ phase still co-existed in the peak aged specimen. The β’ phase was dominated in the peak hardness. It is revealed that the monolayer lying on {1100}Mg act as precursor of β” phase and β’ phase.