Papers by Keyword: Hydrogen Flux

Abstract: The concept for alloy design of Nbbased hydrogen permeable membrane is applied to NbWMo ternary system. The alloying effects of tungsten and molybdenum on the solubility of hydrogen, the resistance to hydrogen embrittlement, the hydrogen permeability and diffusivity are investigated in a fundamental manner. It is found that the addition of tungsten and molybdenum into niobium decreases the hydrogen solubility. As a result, the resistance to hydrogen embrittlement improves and higher hydrogen pressures can be applied to the NbWMo alloy membrane. It is shown that the designed Nb5mol%W5mol%Mo alloy membrane with single solid solution phase exhibits excellent hydrogen permeability together with strong resistance to hydrogen embrittlement. In addition, it is found that the alloying of tungsten and molybdenum with niobium enhances the hydrogen diffusivity. In fact, the activation energy for hydrogen diffusion decreases in the order, pure Nb > Nb5mol%W > Nb5mol%W5mol%Mo.

Abstract: The hydrogen diffuses and accumulates at the stress concentration area like a crack tip and it causes hydrogen embrittlement. To clarify the mechanism of hydrogen embrittlement, it is important to obtain the hydrogen concentration behavior. However, experimental detection is not feasible due to the high diffusivity of hydrogen and numerical analyses have been preceded. In this paper, by using a finite element and finite difference coupled method at which the diffusion analysis is performed by FDM coupled with the stress analysis by FEM, the analyses of hydrogen diffusion were conducted under cyclic loading conditions.

Abstract: The hydrogen solubility and the hydrogen permeability have been measured for Nb-based alloys in order to investigate the alloying effects on the hydrogen diffusivity during hydrogen permeation. It is found that the hydrogen solubility decreases by the addition of ruthenium, tungsten or molybdenum into niobium. The mobility for hydrogen diffusion during hydrogen permeation is estimated from the linear relationship between the normalized hydrogen flux, , and the product of the hydrogen concentration and the difference of hydrogen chemical potential, . It is found that the mobility for hydrogen diffusion during hydrogen permeation is larger for Nb-based alloys than pure niobium, especially at low temperature. The activation energy of the mobility for hydrogen diffusion decreases by the addition of ruthenium, tungsten or molybdenum into niobium.

Abstract: The hydrogen solubility and the hydrogen permeability have been measured for Nb-based alloys in order to investigate the alloying effects on the hydrogen diffusivity during hydrogen permeation. The hydrogen diffusion coefficient during hydrogen permeation is estimated from a linear relationship between the normalized hydrogen flux, , and the difference of hydrogen concentration, C, between the inlet and the outlet sides of the membrane. It is found that the hydrogen diffusion coefficient during the hydrogen permeation is increased by alloying ruthenium or tungsten into niobium. On the other hand, the activation energy for hydrogen diffusion in pure niobium under the practical permeation condition is much higher than the reported values measured for dilute hydrogen solid solutions. It is interesting that the activation energy for hydrogen diffusion decreases by the addition of ruthenium or tungsten into niobium.

Abstract: The hydrogen diffusion coefficients are investigated during the hydrogen permeation through Nb-based hydrogen permeable membranes at high temperature. It is found that the hydrogen diffusion coefficient for pure niobium under practical conditions is much lower than the reported values measured for dilute hydrogen solid solutions. Surprisingly, the hydrogen diffusion is found to be faster in Pd-Ag alloy with fcc crystal structure than in pure niobium with bcc crystal structure at 773K during the hydrogen permeation. It is also found that the addition of Ru or W into niobium increases the hydrogen diffusion coefficient under the practical conditions.