Abstract: The effect of thermal barrier coating (TBC) on low cycle fatigue behavior of cast superalloy Inconel 713 LC has been studied at 900 °C. The TBC consisting of a CoNiCrAlY bond coat and a zirconia (ZrO₂) top coat stabilized by 8% yttria (Y₂O₃) was deposited on the gauge section of cylindrical specimens using the atmospheric plasma spray technique. Cylindrical specimens of Inconel 713LC in as-received condition and with surface treatment were cyclically strained under strain control with constant total strain amplitude in symmetrical cycle at 900 °C in air. Hardening/softening curves, cyclic stress-strain curve and fatigue life data of coated and uncoated material were obtained. The stress response of the TBC coated specimens is lower in comparison with the uncoated specimens. Detrimental effect of surface treatment on the Basquin curve is documented. Specimen sectioning and fracture surface observations revealed fatigue damage mechanisms and help to discuss differences in fatigue behavior of the coated and uncoated superalloy.

Abstract: The work is focused on the study of degradation of ZrO₂ stabilized by Y₂O₃ (YSZ) thermal barrier-coating system with CoNiCrAlY bond coat applied on cast polycrystalline nickel-based superalloy Inconel 713LC. Cylindrical specimens in as-coated conditions were cyclically strained under strain control with constant total strain amplitude in symmetrical cycle at high temperature (900 °C) in air. Coating system YSZ with CoNiCrAlY bond coat were prepared by APS method on blasted surface. The microstructure of TBC was characterized with scanning electron microscopy and energy dispersion X-ray analysis. The coating thickness and hardness profile was measured. Fracture surface, surface relief and polished sections parallel to the specimen axis were examined to study damage mechanisms in coatings under cyclic loading at high temperature. It was find that initiation of the fatigue crack usually occurs on interface YSZ-CoNiCrAlY and the trajectory of the further crack propagation was documented.

Abstract: Cylindrical specimens of Inconel 713LC in as-cast condition and with Al diffusion coating by the CVD technique were cyclically strained under total strain control at 800 °C. Hardening/softening curves, cyclic stress-strain curves, and fatigue life curves are obtained. The coating has a beneficial effect on the Manson-Coffin curve while the fatigue life is reduced in the Basquin representation. The stress response of the coated material is lower in comparison with the uncoated one. Sections parallel to the specimen axis have been examined to study fatigue damage mechanisms.