Abstract: The effects of helium and aging treatment on radiation damage behavior in low activation Fe-Cr-Mn ( W, V) alloy were investigated by electron and helium ion dual-beam irradiation in a high voltage electron microscope. Specimens were aged at 673 K, 823 K and 923 K for 1000, 3000 and 10000 hours. Electron and He ion dual-beam irradiations were performed at 627 K to 10 dpa. M23C6 type carbides were precipitated in the aged specimens, and the amount of the precipitates was increased with increasing aging temperature and aging time. He bubbles were formed during dual-beam irradiation in all of the specimens. The cavity swelling under dual-beam irradiations was increased with increasing the aging temperature and aging time. It was suggested that cavity swelling is closely related to the concentration of solutes such as Cr and C in the matrix, namely cavity growth rate becomes higher with decreasing of the solutes in solution.

Abstract: This paper reported the low activation martensitic steels which are being studied to develop the structural materials in fusion reactors. The steels were based on 9Cr1.5WVTa, but the effect of alloy elements was investigated by changing the amounts of alloy elements or adding other elements. The structure and properties of the steels were studied by tensile experiment, X-ray diffraction, SEM, TEM. Also the metallurgical process and heat treatment effect were discussed.