Abstract: At present many researches are about low density and high strength material, Metal Matrix Composite (MMC) is one kind of high performance material which is very popular and can fit that condition very well. In this study, matrix material is Al alloy and Al2O3 short fiber is reinforcement, volume fractions of Al2O3 short fiber is 10, 15 and 20 %. Manufacture by a low-pressure infiltration method. And the performance is evaluated by microstructure observation, porosity ratio and relative density. It is found that the porosity ratio can be effectively adjusted by the infiltration temperatures and the loads of Al2O3 short-fibres, exhibiting a minimum of 2 for 10% loading at 700°C. Meanwhile, the relative density of composites reached to be a maximum of 98% for 15% loading at 700°C. The low porosity ratio and high density of composites are reasonably attributed to the proper processing techniques.

Abstract: In order to fabricate the metal matrix composites by low-pressure infiltration by gravity casting machine, the preform made from FeCrSi fiber with 40μm and matrix of A336.0 aluminum alloy was used. The volume fraction of fiber in preform was about 20%. The temperatures of die, preform and molten alloy were 200 oC, 400 oC and 750 oC, respectively. By controlling the infiltration of molten aluminum alloy to one direction by using barrier plate, the quantity of pores caused by curling of air degrades dramatically. Molten aluminum alloy was able to infiltrate at low pressure of 0.2MPa. As increasing the pressure, porosity in composites decreased. The composite with no pores was obtained by barrier plate and 0.8 MPa of molten alloy pressure. This composite had high strength at high temperature of 200-400oC.