Papers by Keyword: M50

Abstract: The friction and wear behavior of Si₃N₄, SiC and ZrO₂ sliding against M50 bearing steel under vacuum condition at various applied load were investigated. The results showed that the properties of different ceramic materials cause the difference in wear behaviors. The coefficient of friction was lowest in SiC and M50 bearing steel couple than other cases for graphitic carbon replaced carbidic carbon at the worn layer of SiC. The specific wear rate of ZrO₂ was highest and the lowest was Si₃N₄. The ceramic ball materials have transferred on M50 bearing steel surfaces and tribofilm consistently formed on the ceramic balls wearing surfaces. Dominant wear behaviors for three structural ceramics were adhesion abrasion, plastic deformation and brittle fracture. The couple with Si₃N₄ and M50 showed the best operating conditions for friction and wear resistance under higher applied load.

Abstract: The friction and wear performances of Si3N4 ceramics sliding against bearing steel and to find optimal operating condition against M50 bearing steel couples under high vacuum surroundings were investigated. The tests were studied on the ball-disk machine under different loads and steady sliding velocity. The worn surfaces of tested samples were examined using optical microscope，SEM and XPS. The results showed that the friction coefficient of Si3N4 was decided by the applied load, the critical load of Si3N4’ friction coefficient was 10N applied load; The critical load of Si3N4’ specific wear rate was 5N applied load, the specific wear rate of Si3N4 drop rapidly as the applied load exceeded the critical load; The dominant wear mechanisms of Si3N4 ceramics were adhesion wear, brittle facture and furrow wear in vacuum.