Papers by Keyword: Manson-Coffin Law

Abstract: The material quality, the deformation rate, the temperature and the stress state influence mechanical behaviour and properties of different materials. Due to this great variety of the influencing factors we do not have one model of general validity describing the behaviour of materials, but we have to use a great number of material constants in order to characterize the properties. The exponents of the Manson-Coffin, the Basquin and the Paris-Erdogan laws were applied for the verification of the connection among the fatigue fracture types. Own measured values and test results can be found in the literature were used for the illustration of the connections. “Fracture surface”-s were determined for characterizing of different steel grades and their welded joints. It can be concluded that “fracture surface”-s are suitable for the describing of the fracture behaviour and the conversion of different fracture parameters of steels.

Abstract: Cyclic strain control tests have been performed on cylindrical specimens of cast polycrystalline Inconel 792-5A superalloy at 23, 500, 700 and 800 °C in laboratory atmosphere to study the effect of temperature on the fatigue behavior. Cyclic hardening-softening curves and fatigue life curves were measured. Scanning electron microscopy was used to investigate the surface relief. Low amplitude straining was characterized by saturation of the stress amplitude. In room temperature high amplitude straining cyclic hardening was followed by marked saturation. Pronounced continuous hardening until failure was observed at 500 °C. Initial cyclic hardening was followed by softening at 800 °C. A systematic shift of the Manson-Coffin and of the Basquin curves to lower fatigue lives was found when temperature was increased. Fatigue cracks were observed to initiate from surface slip markings at all temperatures.