Papers by Keyword: Metal Induced Crystallization

Abstract: A viscous Nickel (Ni) solution was applied on amorphous Si films by spin coating and its effect on the crystallization of amorphous Si films was investigated with a two-step annealing process. The experimental results show that with the help of the two-step annealing, the crystallization of the film can take place at 500oC. At the same time, the crystalline fraction gets up to 79.4% after annealing at a high temperature of 520oC and the grain size of the polycrystalline Si films is approximately 200 nm.

Abstract: In this work metal induced crystallization (MIC) using nickel (Ni) was employed to obtain poly-Si by crystallization of amorphous films for application as active layer in TFTs. Ni layers with thicknesses of 0.5 nm, 1 nm and 2 nm were used to crystallize the silicon. The TFTs were produced with a bottom gate configuration using a multi-layer Al2O3/TiO2 insulator produced by atomic layer deposition (ALD) as gate dielectric. The best performances of the TFT produced were obtained when using very thin Ni layers for the crystallization. This is attributed to a lower metal contamination and to the enhancement of grain size, as a result of the lower nucleation density achieved, when using the thinnest Ni layer. Devices that exhibit effective mobility of 45.5 cm2V-1s-1 and an on/off ratio of 5.55×104 were produced using a 0.5 nm Ni layer to crystallize the active channel area.