Papers by Keyword: Nanocrystalline (NC) Structure

Abstract: Amorphous-nanocrystalline Ti49.4Ni50.6 alloy in the shape of a disc 20 mm in diameter has been successfully produced using high pressure torsion (HPT). Application of HPT and annealing at temperatures of 300–550°C resulted in formation of a nanocrystalline (NC) structure with the grain size (D) about 20–300 nm. The HPT samples after annealing at Т = 400°C with the D= 20 nm possess high yield stress and high ultimate tensile strength (more than 2000 MPa). There is an area of strain-induced transformation B2-B19’ on the tensile curve of the samples with the grain size D =20 nm. The stress of martensitic transformation (σm) of samples is 450 MPa, which is three times higher than σm in the initial coarse-grained state (σm ≈ 160 MPa). The HPT samples after annealing at Т = 550°C with the D= 300 nm possess high ductility (δ>60 %) and high ultimate tensile strength (about 1000 MPa).