Papers by Keyword: Noncombustible Magnesium Alloy

Abstract: Noncombustible magnesium alloy AMC602 (Mg-6mass%Al-2mass%Ca) extruded sheet of 2.0mm thickness was successfully welded using a fiber laser welding process at welding speed of 10m/min at 3kW laser power. Tensile strength of the welded joint was about 82 to 88% of that of the base metal. Vickers hardness, tensile strength and micro structural properties are also discussed.

Abstract: Effect of mean stress on fatigue strength at N=107 of non-combustible magnesium alloy AMX602B(X=Ca) was investigated. Rotating bending fatigue test and tension-compression fatigue test were carried out on specimens with a small hole or crack. It was clarified that the fatigue strength at N=107 of the specimen with the small hole was about 30-150% higher than that of the specimen with the small crack within the range of σm=0~100MPa. This is the reason why the fatigue strength at N=107 of the specimen with the small hole can be not threshold condition for crack propagation but crack initiation. The fatigue strength at N=107 of the specimens with the small hole decreased within the range of σm=100~195MPa due to a static small crack initiating from the small hole at first loading. The effect of mean stress on fatigue strength at N=107 both oh the specimens with the small hole and crack could be estimated using modified Goodman diagram.

Abstract: Noncombustible Mg-8Al-2Ca rods were processed by RD-ECAP. The magnesium alloy rod had Mg matrix and Al2Ca second phase. Grains with about 20 μm in diameter were observed in the matrix of the raw materials. The grains in matrix had no anisotropy. On the other hand, positions of second phase particles had anisotropy and the second phase particles formed lines. The samples processed by RD-ECAP had no crack and the samples had 20mm diameter. Grains in matrix of the 4 pass RD-ECAP sample had no anisotropy and the grains had under about 5 μm in diameter. The second phase particles had round shapes and were uniformly distributed as compared with the raw material rod. Therefore, the RD-ECAP is useful for forming noncombustible Mg-8Al-2Ca alloy with fine-grains.