Papers by Keyword: Physical Modelling

Abstract: Today physical modelling is a commonly used tool in modelling metallurgical processes. It can be applied both in steel metallurgy and non-ferrous metals metallurgy processes. It gives the opportunity to determine the hydrodynamic conditions of the processes. Although, the flow of mass and gas is not totally presented by such modelling, this kind of research is very often and willingly used. That is because it is really difficult to conduct experimental research in industrial conditions. Typically water is used as a modelling agent, so the physical modelling is not as expensive as the one carried out in industrial conditions. To obtain representative research from physical modelling the physical models have to be built according to the strict rules coming from the theory of similarity. The results obtained from the experimental test on the physical model, after verification, can be transferred to the real conditions. The article shows the obatined results coming from physical modelling of the steel production process. In the Institute of Metals Technologies of Silesian University of Technology the appropriate test stand was built to simulate the steel flow and mixing in the ladle. The visualization results have been presented. To simulate processing condition during aluminium refining additional test stand was also built. The exemplary results have been shown for different flow rate of gas, rotary impeller speed and different shapes of impellers. All presented results have been discussed and presented for the perspectives of further research.

Abstract: The paper presents the results of physical modelling of the plastic deformation of the Mg/Al bimetallic specimens using the Gleeble 3800 simulator. The plastic deformation of Mg/Al bimetal specimens characterized by the diameter to thickness ratio equal to 1 was tested in compression tests. The aim of this work was determination of the range of parameters as temperature and strain rate that mainly influence on the plastic deformation of Mg/Al bars during metal forming processes. The tests were carried out for temperature range from 300 to 400°C for different strain rate values. The stock was round 22.5 mm-diameter with an Al layer share of 28% Mg/Al bars that had been produced using the explosive welding method. Based on the analysis of the obtained testing results it has been found that one of the main process parameters influencing the plastic deformation the bimetal components is the initial stock temperature and strain rate values.