Papers by Keyword: Poly(ether sulfone)

Abstract: Microfibers have huge potential applications in many fields due to their unique properties. However, the high performance thermoplstic microfibers were rarely reported. In this work, Poly (ether sulfone) Microfibers were first successfully prepared by melt extrusion of immiscible blends of PES, Polyamide 6 ( PA6 ), and subsequent removal of PA6 component. The morphologies of the PES microfibers were characterized by SEM. The experimental results showed the PES microfibers exhibited interconnected structures between the fibers and the average diameter was about 150 nm. The present PES microfiber may be applied to the development of ultrafiltration membranes materials.

Abstract: Poly(ethersulfone)s carrying pendant sulfonated imide side group. The first step in the preparation involved nitration of poly(ethersulfone) (ultrason^®-S6010), with ammonium nitrate and trifluoroacetic anhydride resulting in the nitrated poly(ethersulfone) (NO₂-PES). In the second step, the nitro groups on polymer were reacted with tin(II)chloride and sodium iodide as reducing agents for creating the amino poly(ethersulfone) (NH₂-PES). The imide-poly(ethersulfone)s (IPES) were obtained by reaction of phthalic anhydride and the amino-poly(ethersulfone) with triethyl amine. The sulfonated imide-poly(ethersulfone)s (SIPES) were prepared by chlorosulfonic acid. The different degrees of sulfonated imide units of poly(ethersulfone) were successfully synthesized by an optimized condition. The Sulfonated imide-poly(ethersulfone)s (SIPES) were studied by FT-IR, ¹H-NMR spectroscopy and thermo gravimetric analysis(TGA). Sorption experiments were conducted to observe the interaction of sulfonated polymers with water. The ion exchange capacity (IEC) and proton conductivity of SIPES membranes were evaluated with increase of degree of sulfonation. The water uptake of synthesized SIPES membranes exhibit 30 ~ 65 % compared with 28 % of Nafion 211^®. The SIPES membranes exhibit proton conductivities (25 °C) of 1.21 ~ 2.62´10^-3 S/cm compared with 3.37´10^-3 S/cm of Nafion 211^®.

Abstract: Organic-inorganic Nano composite membranes were prepared by Sulfonated amine-poly(ether sulfone)s (S-APES)s and SiO2. S-APESs were prepared by nitration, reduction and sulfonation of poly(ether sulfone) (ultrason®-S6010). Poly(ether sulfone) was reacted with ammonium nitrate and trifluoroacetic anhydride to produce the nitrated poly(ether sulfone), and was followed by reduction using tin(Ⅱ)chloride and sodium iodide as reducing agents to give the amino-poly(ether sulfone). The S-APES was obtained by reaction of 1,3-propanesultone and the amino-poly(ether sulfone) (NH2-PES) with sodium methoxide. The different degrees of nitration and reduction of poly(ether sulfone) were successfully synthesized by an optimized process. Organic-inorganic nano composite membranes were obtained by mixing S-APES (45 %) with hydrophilic SiO2 (20 nm, 4-10 %) obtained by sol-gel process. Different contents of SiO2 of the S-APES were studied by FT-IR, 1H-NMR spectroscopy, differential scanning calorimetry (DSC), and thermo gravimetric analysis (TGA). Sorption experiments were conducted to observe the interaction of sulfonated polymers with water and methanol. The ion exchange capacity (IEC), a measure of proton conductivity, was evaluated. The nano composite membranes exhibit conductivities (25 °C) from 3.51 x 10-3 to 4.10 x 10-3 S/cm, water swell from 57.25 to 60.50 %, IEC from 0.68 to 0.73 meq/g, and methanol diffusion coefficients from 2.81 x 10-7 to 3.33 x 10-7 cm2/S at 25 °C.

Abstract: Poly(ether sulfone)s (PES) containing 25-75 mol % valeric acid were prepared with bisphenol A, bis(4-chlorophenyl)sulfone and 4,4-Bis(4-hydroxylphenyl)valeric acid using potassium carbonate in DMAc (dimethylacetamide) at 160 °C. Copolymers containing carboxylacid group were reduced to hydroxy group by BH3 solution 1M in THF and NaBH4 co-catalyst. Sulfonated poly(ether sulfone)s (S-PES) were obtained by reaction of 1,3-propanesultone and the reduced copolymer (PES-OH) with potassium t-butoxide. A series of copolymers were studied by 1H-NMR spectroscopy, differential scanning calorimetry (DSC), and thermo gravimetric analysis (TGA). Sorption experiments were conducted to observe the interaction of sulfonated polymers with water and methanol. The S-PES membranes exhibited proton conductivities from 1.20  10-3 to 3.40  10-3 S/cm, water swell from 12.25 to 31.50 %, IEC from 0.43 to 0.72 meq/g and methanol diffusion coefficients from 3.60  10-7 to 4.90  10-7 cm2/S at 25 °C.