Papers by Keyword: Polystyrene Resin

Abstract: Composite electromagnetic wave absorbers made of a soft magnetic material (permalloy or sendust) and polystyrene resin were investigated [1]. The volume mixture ratio of magnetic material was varied in the range from 18 vol% to 75 vol%. The composites with the low volume mixture ratio of soft magnetic material absorbed more than 99 % of electromagnetic wave power in the frequency range from 1 GHz to 10 GHz. The values of the real part
r’ of the relative complex permeability
r * for both magnetic materials were less than unity at frequencies above approximately 6 GHz as the volume mixture ratio of magnetic material increased. This result suggests the possible realization of an electromagnetic wave absorber that can operate above 10 GHz.

Abstract: The frequency dependences of the complex permeability μ r*, complex permittivity ε r*, and return loss were investigated for composite electromagnetic wave absorbers made of soft magnetic materials (permalloy or sendust) and polystyrene resin. For permalloy, two types of particle shape were used: grain-type or flake-type. The volume mixture ratio of magnetic materials was varied in the range from 40 % to 70 %. The values of the real part μ ’ and imaginary part μ ” of μ r * increased with increasing mixture ratio of magnetic materials. The frequency dependence of μ r * for flake-type permalloy composite was similar to that for sendust composite. All absorbers showed the absorption of electromagnetic waves in the frequency range above 1 GHz.