Papers by Keyword: Preheated Machining

Abstract: In this paper, the tool life and tool wear performance of PCBN tool in end milling of AISI D2 hardened steel under room and preheated machining conditions is presented. The tool life and tool wear patterns were examined through tool maker microscope and scanning electron microscope. The results show that the dominant modes of tool wear observed were flank wear, chipping, and notch wear. The main wear mechanisms were abrasion, adhesion, and diffusion promoted by high stress and cutting temperature. It was also observed that longer tool life and higher volume metal removed could be achieved when employing higher preheating temperature.

Abstract: This study was conducted to investigate the effect of preheating through inductive heating mechanism in end milling of AISI D2 hardened steel (60-62 HRC) by using coated carbide tool inserts. Apart from preheating, two other machining parameters such as cutting speed and feed were varied while the depth of cut constant was kept constant. Tool wear phenomenon and machined surface finish were found to be significantly affected by preheating temperature and other two variables. End milling operation was performed on a Vertical Machining Centre (VMC). Preheating of the work material to a higher temperature range resulted in a noticeable reduction in tool wear rate leading to a longer tool life. In addition, improved surface finish was obtained with surface roughness values lower than 0.4 μm, leaving a possibility of skipping the grinding and polishing operations for certain applications.