Abstract: This article is focused on optimization of fundamental utility properties and technological process of advanced low alloy steel 15NiCuMoNb5 used for power engineering mainly for production of large capacity steam boilers. Consequently problem critical locality in weld after post weld heat treatment is studied. Optimization of welding technology is proposed. Fracture behaviour of welded joint made from boiler plates 80 mm in thickness of 15NiCuMoNb5 type steel after N + T PWHT regime after welding procedure were studied. Stable crack growth measurement and evaluation of fracture toughness of base material as well as weld metal in temperature region from 0 up 350°C were carried out. Unstable cleavage fracture and fracture toughness KJc of both parts of welded joint at test temperatures cover the transition region were evaluated. The reference temperature T0 approach was used for evaluation of temperature dependence of fracture toughness in transition range.

Abstract: The master curve has evolved into a mature technology for characterizing the fracture toughness transition of ferritic steels. However, it is well known that the master curve reference temperature (To) values estimated from small laboratory specimen may be biased low due to loss of crack-tip constraint. To quantify such variations of To resulting from differences of crack-tip constraint of testing specimen, two-parameter fracture mechanics approaches are employed in the present study. In this context, fracture toughness test and 3-dimensional finite element (FE) analysis for several standard and nonstandard test specimens are performed to quantify relationship between variations of To and constraint parameters and to find best constraint parameter representing effect of crack-tip constraint on To values evidently. Based on testing and present FE results, To and constraint parameter loci are constructed and engineering To correlation models considering crack-tip constraint are suggested