Abstract: In order to investigate the influence of grain size on notch sensitivities in fatigue of a fine-grained carbon steel, rotating bending fatigue tests were carried out using specimens with a V-grooved circumferential notch of commercial fine-grained carbon steel with grain size of 6.5µm. The results were compared with those of a larger grain sized carbon steel (grain size: 20 µm) and the notch sensitivities were evaluated based on Linear notch mechanics proposed by Nisitani. Notch sensitivities for both of fatigue limits for a crack initiation and its propagation of the fine grained steel were high. The results were discussed from the view points of the size of area related to crack initiation and the crack growth resistance.

Abstract: Rotating bending fatigue tests were carried out for maraging steels with different grain size in moist air in order to investigate the effects of humidity, grain size and reversion austenite on fatigue strength of the steel. Fatigue strength was decreased by humidity, and the decrease in fatigue strength was large in larger grain sized steel. Both of the initiation and propagation of a crack were promoted by humidity. Many cracks initiated at the specimen surface and intergranular cracks were observed at specimen surface and on fracture surface when humidity was high. The decrease in fatigue strength by humidity was suppressed by formation of reversion austenite.