Papers by Keyword: Semi-Insulating Material

Abstract: The behavior of the D1 center in semi-insulating 4H-SiC substrates revealed by low-temperature photoluminescence was investigated after post-growth high temperature anneals between 1400 and 2400oC. The influence of different post-anneal cooling rates was also studied. The optical signature of D1 was observed up to 2400oC with intensity maxima at 1700 and 2200oC. We propose that the peak at 1700°C can be related to the formation and subsequent dissociation of SiC native defects. It was found that changes in the post-annealing cooling rate drastically influence the behavior of the D1 center and the concentrations of the VC, VSi, VC-VSi and VC-CSi lattice defects.

Abstract: Undoped 6H- and 4H-SiC crystals were grown by Halide Chemical Vapor Deposition (HCVD). Concentrations of impurities were measured by various methods including secondary-ion-mass spectrometry (SIMS). With increasing C/Si ratio, nitrogen concentration decreased and boron concentration increased as expected for the site-competition effect. Hall-effect measurements on 6H-SiC crystals showed that with the increase of C/Si ratio from 0.06 to 0.7, the Fermi level was shifted from Ec-0.14 eV (nitrogen donors) to Ev+0.6 eV (B-related deep centers). Crystals grown with C/Si > 0.36 showed high resistivities between 1053 and 1010 4cm at room temperature. The high resistivities are attributed to close values of the nitrogen and boron concentrations and compensation by deep defects present in low densities.