Abstract: Si electrode with different amount of polymer binder was fabricated by ball milling. With increasing of polymer content, not only porosity but also the first charge capacity of Si electrode was increased. The Si electrode enhanced electrical conductivity showed high first capacity of 3644mAh/g and improved cycle performance. Si electrode having good electrochemical property could be fabricated by controlling amount of polymer.

Abstract: Si film electrodes for Li micro-film batteries were fabricated on a Cu substrate and a Ci/Cu film. In the structural properties, FE-SEM observation demonstrated difference in surface morphologies of Si films with different under layers. Surface of the Si film deposited consists of clusters and average size of the cluster was 165 nm for Si/Cu film and 80 nm for Si/C/Cu film. Si film has amorphous phase in spite of different under layers; Cu substrate and C/Cu film. In the electrochemical properties, the carbon-inserted film showed a good cycleability compared with Si/Cu electrode. It is believed that the insertion of carbon film as a buffer film absorbed the stress generated during charge-discharge process and improved cycle performance of Si anode electrode.

Abstract: Si film electrodes for Li micro-film batteries were fabricated on a Cu substrate and a Ni/Cu film. In the structural properties, Si film had an amorphous structure, while the crystallinity of Ni buffer film was improved after annealing. FE-SEM observation demonstrated differences in surface morphologies of Si films fabricated with different methods. In the electrochemical properties, the Ni-inserted film showed the largest initial charge and discharge capacity, and the cell with annealed Si/Ni/Cu film showed good cycleability. It is believed that the insertion of Ni film as a buffer film improved the charge and discharge capacity owing to the enhancement of adhesion between Si film and Cu substrate.