Abstract: Textured SrBi2Nb2O9 (SBN) ceramics were fabricated by templated grain growth (TGG) method. The plated-like SBN particles with shape anisotropy prepared by molten salt method were used as the templates. The SBN powders prepared by conventional solid (CS) reaction were used as matrix powders. It was found that the textured SBN ceramics can be obtained by TGG method. The grain orientation (Lotgering factor, f) increased with the increase of sintering temperature and content of the templates. The textured SBN ceramics with f=0.86 could then be obtained after sintering at 1300 °C for 3 h with 20wt.% templates. The relative density keeps rising with increasing temperature until it reaches a peak value 91.22% at the sintering temperature 1300°C, after which it decreases.

Abstract: Vanadium-substituted strontium bismuth niobate, SrBi2Nb2-xVxO9 (SBNVx), ceramics were synthesized by a low-temperature ceramic fabrication process; their electric properties were characterized, and grain orientation effects on their electric properties were also investigated using a hot-forging (HF) method. Resonance characteristics of the (33) and (15) modes of grain-oriented SBNV0.1 (HF) showed relatively high electromechanical coupling factors of k33=0.272 and k15=0.151 as well as piezoelectric constants of d33=31.7 pC/N and d15=24.8 pC/N. The temperature dependences of the resonance frequency (TC-f) of the (33) and (15) modes of the SBNV0.1(HF) ceramics were -16.5 ppm/°C and –25.5 ppm/°C, respectively.