Papers by Keyword: Three Sheets

Abstract: Resistance spot welding is used extensively in auto industry. Every commercial vehicle has 4000-5000 spot welds. The weld ability, performance, and reliability are therefore important issues in design. In this paper, we studied weld nugget formation and failure behavior of three-sheet 5052 aluminum alloy resistance spot welds. The Peltier effect between the Cu-Al (the electrode and the Al worksheet) to the nugget formation was noticed. The mechanical strength and fracture mode of the weld nuggets at the upper and lower interfaces were studied using tensile shear specimen configuration. Three failure modes were identified, namely, interfacial, mixed, and pull-out. The critical welding time and critical nugget diameter corresponding to the transitions of these modes were investigated. Finally, an empirical failure load formula for three-sheet weld similar to two-sheet spot weld was developed.

Abstract: The joinability of three aluminium alloy sheets using a self-piercing rivet was evaluated from a finite element simulation and experiment. The self-piercing riveting is hopeful as replacement of spot resistance welding generally used for steel sheets, because it is not easy to apply the resistance welding to joining of three aluminium alloy sheets due to the high thermal conductivity. Defects in the riveting are categorized into the penetration through the lower sheet, the necking of the lower sheet and the short overlap of sheets to obtain optimum joining conditions. The penetration and the necking are caused by small total thickness. The short overlap tends to occur as the ratio of lower sheet and total thickness is small. In addition, the cross-tension test was simulated by the finite element method to evaluate the joint strength.