Papers by Keyword: Tungsten Carbide Material

Abstract: Polycrystalline diamond (PCD) exhibits a thermal conductivity similar to that of the electrically conductive chemical vapor deposition diamond (EC-CVD diamond) found to function as zero-wear electrodes at short pulse duration. In this study, PCD was used as electrodes applied to EDM on tungsten carbide. Two kinds of PCD (CTB-010 and CTH-025) with a flat surface were used. The wear of the PCD electrodes was about 1.5% for very short pulse duration such as te=1μs, but it was zero wear at te=30μs, though the wear of a Cu-W electrode was 10% even on the machine recommended conditions for the low wear. EDM experiment using a V-shaped PCD electrode with an included angle of 45° was also carried out and the performance was compared with the case using a V-shaped Cu-W electrode. Under the conditions of a no load voltage of 60V, a set peak current of 2A, and a medium pulse duration of te=15μs, there was no wear on PCD electrodes when observed under the SEM, whereas a 50μm-deep wear on the Cu-W electrodes even under the machine recommended condition for the low wear was observed.

Abstract: Electro-discharge grinding (hereafter called ED-grinding) was carried out with a trial manufactured metal bond diamond wheel containing electrically conductive diamond grits (hereafter called EC-D-grits-wheel). In this research two effects i.e. removal action of workpiece by electrical discharge machining, and an in-process dressing action of the cutting edges on the grits are expected to take place. The results of ED-grinding with EC-D-grits-wheel (f100mm, SDE120Q80M) on tungsten carbide indicated a significant decrease of 21% in the grinding force, when the set discharge current was increased from 0A to 12A. It was also clarified from the alternative-grinding test with and without an electro-discharge action that stable grinding characteristics along with a reduced grinding force could be achieved in the case of the EC-D-grits-wheel with the electro-discharge action. High-speed camera photographs indicated that a stable discharge condition was achieved.