Abstract: The mechanical activation was employed to study the phase evolution of the Mg–TiO2–CaHPO4–CaO nanocrystalline system. The powders mixture with certain weight percent was grinded. Thermal annealing process at 650°C, 900°C and 1100°C temperatures resulted in generation of different compounds like MgTiO3/MgO/Hydroxyapatite (HAp) and MgTiO3/MgO/β-TCP and MgTiO3/Mg2TiO4/MgO/β-TCP, respectively. The compounds were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and energy dispersive X-ray spectroscopy (EDX). The consequences of XRD analysis revealed that by increasing temperature, some composites with different morphological and structural features were detected. Beside, due to decomposing of HAp around 800°C, HAp converted to whitlockite (β-TCP) with growth of temperature. According to SEM and TEM observations, it was found that the synthesized powder contained large agglomerates which significant content of finer particles and agglomerates with spherical morphology. Because magnesium titanates based dielectric materials are useful for electrical applications, the electrical property of HAp has been proved, and the incorporation of these materials could result in new nanocrystalline dielectric materials.

Abstract: Impedance spectroscopy was used to monitor the non-isothermal crystallisation of a phosphate phase in bulk samples of a glass with the molar composition 0.45SiO2–0.36MgO– 0.09K2O–0.1(3CaO⋅P2O5), intended for biomedical applications. The K+ alkali ions are probably the main charge carriers in glass of this composition [1]. Impedance spectra were obtained as a function of temperature, following non-isothermal heat treatments at 2°Cmin-1. It is shown that suitable analysis of impedance spectra can be used to evaluate the crystallization peak of a orthophosphate phase, Ca9MgK(PO4)7. Results obtained by this method are comparable to those obtained by differential thermal analysis (DTA) of the corresponding glass frits. Impedance spectroscopy is thus suitable to study the crystallization of bulk samples, and can be used both with variable temperature and under isothermal conditions.

Abstract: Impedance spectroscopy was used to measure the changes of electrical properties during the isothermal crystallisation of the phosphate phase in bulk samples of a glass with nominal molar composition (3CaO.P2O5)20(SiO2)35(MgO)38.354(K2O)6.646, developed for biomedical applications. Crystallization studies were performed in isothermal conditions at 800°C and 860°C, and were monitored by impedance spectroscopy. XRD shows that a stable orthophosphate phase, Ca9MgK(PO4)7 crystallizes at about 860°C, after formation of earlier phosphate precursors formed at lower temperatures, namely oxyapatite (Ca5(PO4)3O) and tricalcium phosphate (Ca3(PO4)2). The conductivity of bulk glass samples decreases at 800°C, as the phosphate precursors phases crystallize. The opposite trend is observed on crystallizing the orthophosphate phase, at 860°C.