Study on Kinetics of Nano-Ni(OH)2 Powder Ethanol Desorption Process


Article Preview

This paper studies on the thermal analysis kinetics of nanometer powders ethanol desorption process.The DTA-TG-DTG curves obtain by SDT 2960 Simultaneous DSC-TGA analysis apparatus. Under the condition of N2 atmosphere operation and rise temperature velocity was 10°C·min-1. The mechanism function is used to calculate the kinetics factors. Reaction progression n was obtained by calculation of the kissinger peak shape factor method. The results showed that the apparent activation energy of nano-Ni(OH)2 was 73.210 kJ·mol-1, the pre-exponential factor was 2.349×1012, the reaction progression was obtained as 1.2767, the kinetic equation is



Edited by:

Z.S. Liu, L.P. Xu, X.D. Liang, Z.H. Wang and H.M. Zhang




F. Pan et al., "Study on Kinetics of Nano-Ni(OH)2 Powder Ethanol Desorption Process", Advanced Materials Research, Vol. 1015, pp. 509-512, 2014

Online since:

August 2014




* - Corresponding Author

[1] Rongzu Hu, Qizhen Shi. Thermal Analysis Kinetics[M]. Beijing: Science Press, 2001, 65. In Chinese.

[2] Zhengqian Cai. thermal analysis[M] Beijing: Higher Education Press, 1993, 68-104, 113-117. In Chinese.

[3] Boling Yu, Jiaodong Dong. Practical thermal analysis[M] Beijing: Textile Industry Press, 1999, 151-158. In Chinese.

[4] Chengyan Liu, Zaiyuan Li. [J]. Journal of Molecular Science, 2007(1):66-68. In Chinese.

[5] Panwei Gong, Zaiyuan Li. [J]. Journal of Molecular Science, 2010(7): 307-311. In Chinese.

[6] Shiping Li, Wenge Zhou, Hongsen Xie. [J]. Bulletin of Mineralogy Petrology and Geochemistry, 2001, 20(3): 194-1. In Chinese.

[7] Zaiyuan Li, Kai Yu, Yun Gao, Jie Liu, Duo Jin, and Yuchun Zhai. [J]. Marerials Science Forum , 2011, 694: 769-772.

[8] Zaiyuan Li, Zhai Yuchun, Pang Myongil. [J]. Advanced Materials Research, 2011, 284-286: 726-729.

[9] Yingjiao Liang, Yinchang Che. [M]. Shenyang: Northeastern university press, 1993. 1-486. In Chinese.

[10] Shulan Wang, Yingjiao Liang. physical chemistry[M]. Beijing: metallurgical industry press, 2007. 200-217. In Chinese.