Preparation of Red Long Afterglow Phosphorescent Material CaTiO3: Pr3+


Article Preview

CaTiO3:Pr3+ was prepared by high temperature solid state reaction and measured by SEM, XRD, excitation and emission spectra. The samples obtained possessed orthorhombic crystal structure of CaTiO3, belonging to Pbnm space group. Excitation spectra of the samples were broad band, their peaks and shoulder peaks were located at about 335nm, 379nm respectively. Emission spectra were single narrow band, emission peaks were located at about 602nm, corresponding to emission of 1D2→3H4 of Pr3+ion. The addition of Eu3+and Dy3+ as co-activator led phosphorescent intensity to greatly enhance, the addition of AgNO3 as ion compensator made the samples material pink and vibrant.



Advanced Materials Research (Volumes 11-12)

Main Theme:

Edited by:

Masayuki Nogami, Riguang Jin, Toshihiro Kasuga and Wantai Yang






M. Li et al., "Preparation of Red Long Afterglow Phosphorescent Material CaTiO3: Pr3+", Advanced Materials Research, Vols. 11-12, pp. 217-222, 2006

Online since:

February 2006




[1] N. Kodama, T. Takahashi, M. Yamaga, et al: Appl. Phys. Lett. Vol. 75 (1999), p.1715.

[2] J. Qiu, M. Kawasaki, K. Tanaka, et al: J. Phys. Chem. Solids. Vol. 59 (1998), p.1521.

[3] Y.H. Liu, Z.L. Tang, Z.T. Zhong, et al: J. Eur. Ceram. Soc. Vol. 23 (2003), p.175.

[4] Z.P. Yang, W.J. Wang, Z. Guo, et al: J. Optoelectronics Later. Vol. 15 (2004), p.332.

[5] H.K. An, S.H. Kang and K.S. Suh: J. Mater. Sci.: Mater. Electronics. Vol. 12 (2001), p.157.

[6] T. Kinoshita, M. Yamazaki, H. Kawazoe, et al.: J. Appl. Phys. Vol. 86 (1999), p.3729.

[7] Y.L. Liu, Y.Y. Li and Y.S. Yang: J. Jinan University (Natural Science) Vol. 17 (1996), p.65.

[8] G.X. Zhu, G. X, Zhuang and Y.M. Jiang: J. Zhanjiang Normal College Vol. 24 (2003), p.46.

[9] Z.P. Yang, Z. Guo, W.J. Wang, et al: J. Functional Mater. Devices. Vol. 9 (2003), p.473.

[10] R.R. Martin, H. Tamaki and S. Matsuda: US Patent US005650094A (1997).

[11] Z.P. Yang, S.C. Zhu, Z. Guo, et al: J. Chinese Rare Earth Soc. Vol. 20 (2002), p.42.

In order to see related information, you need to Login.