Influence of Quench and Tempering Temperature on the Microstructure and Properties of 20SiMn2MoVA Steel

Abstract:

Article Preview

Using optical microscopy、impact and tensile test,Study the effects of different quenching and tempering temperature on the microstructure and mechanical properties of the steel 20SiMn2MoVA.The results showed that, at the test temperature range,with the rise of quenching temperature the tensile strength of steel 20SiMn2MoVA declining, Low-temperature impact energy along with the quenching temperature rise was increasing. After quenching at 920°Cand tempering at different temperatures, with increasing tempering temperature, the tensile strength of the material showed a declining trend, impact toughness values were rising trend has decreased, 220°Ctempered impact toughness appear peak. Below 300°C tempering is tempered martensite and a small amount of residual austenite; More than 300°C tempering, residual austenite begins to decompose, carbide separeated out, 400°Ctempering is tempered flexor s body. Test material at 920°Cafter quenching and tempering 220°C, has good strength and toughness, specific properties: tensile strength 1506 MPa and temperature impact toughness Akv 35.6J.

Info:

Periodical:

Advanced Materials Research (Volumes 1120-1121)

Edited by:

Antonio Apicella

Pages:

978-982

DOI:

10.4028/www.scientific.net/AMR.1120-1121.978

Citation:

X. H. Zhang et al., "Influence of Quench and Tempering Temperature on the Microstructure and Properties of 20SiMn2MoVA Steel", Advanced Materials Research, Vols. 1120-1121, pp. 978-982, 2015

Online since:

July 2015

Export:

Price:

$38.00

* - Corresponding Author

[1] T. Shi, W. F. Gao, X. W. Lei, Effect of "Zero Time Holding" Quenching on Impact Property of 20SiMn2MoV Steel, J. Material & Heat Treatment, 2011, 40(22): 199-202.

[2] Z. Q. Zhang, Z. G. Yu, G. X. Li, X. P. Ma, Reason of 20SiMn2MoVA Steel with Low Impact Property, J. Materials for Mechanical Engineering, 2010, 34(7): 77-79.

[3] Z. G. Yu, 20SiMn2MoVA Steel Hydrogen Brittle Cracking Analysis and Decontamination, J. PTCA (Part A: Physical Testfing), 2003, 39(7): 338-340.

[4] Y. Zhang, Study on the Normalized Structure and Property of Steel 20SiMn2MoVA and 20CrMnSiMoVA, J. Heat Treatment of Metals, 1984, 9(11): 31-38.

[5] Y. J. Yin, Y. F. Zhu, X. P. Zhao, Y. Zhang, M. Zhang, J. Liu, Impact Property of 20SMin2MoV Steel at Low Temperature, J. Heat Treatment of Metals, 2006, 31(4): 12-15.

[6] W. F. Gao, X. W. Lei, T. Shi, The effect of subcritical quenching on the low-temperature toughness of the 20SiMn2MoV steel, J. CPM, 2011, 39(9): 1-4.

[7] Y. F. Zhu, F. Y. Wang, H. H. Zhou, G. Wang, B. Z. Jiang, Stepping-quenching-partitioning treatment of 20SiMn2MoVA steel and effects of carbon and carbide forming elements, J. Sci. China Tech. Sci., 2012, 55(7): 1838-1843.

DOI: 10.1007/s11431-012-4884-8

[8] G. H. Wu, Cause Analysis and Preventive Measures of Line Hardware Frost Crack, J. Electric Power Construction, 2007, 28(2): 73-75.

[9] C. N. Luo, T. Li, Development of High Strength Hardware, J. Electric Power Construction, 2007, 28(2): 73-75.

In order to see related information, you need to Login.