Preparation of Magnetic Abrasive by Sintering Method


Article Preview

In this paper, ferrosilicon powder was used as the ferromagnetic phase, corundum powder as the abrasive phase, high temperature inorganic binder as the adhesive, and after the ferrosilicon powder was modified, a series of magnetic abrasive was obtained by sintering method. Scanning electron microscope (SEM) and Energy dispersive spectrometer (EDS) were respectively used to characterize the morphology and elemental composition of magnetic abrasive. and through experiments carried out on the magnetic abrasive grinding performance testing and durability analysis. The experimental results showed that the magnetic abrasive prepared had good polishing ability and longer using time, and the surface roughness of the grinding sample can reach 0.12μm and the using time is up to 25 min.



Edited by:

Qiusheng Yan, Jiabin Lu, Jun Wang and Hang Gao






Z. D. Zhao et al., "Preparation of Magnetic Abrasive by Sintering Method", Advanced Materials Research, Vol. 135, pp. 382-387, 2010

Online since:

October 2010




[1] T. Shinmura, F.H. Wang, T. Aizawa: Journal of Japan Society for Precision Engineering Vol. 59(1993), pp.41-45.

[2] T. Shinmura, T Aizawa: Journal of Japan Society for Precision Engineering Vol. 54(1988), pp.124-129.

[3] T. Shinumura, K. Takazawa: Bull. Japan Soc. of Prec. Engg. Vol. 19(1985), pp.289-291.

[4] T. Shinumura, K. Takazawa And E. Hatano: Japan Bull. Japan Soc. Engg. Vol. 18(1984), pp.347-348.

[5] H. Yamaguchi, T. Shinmura: Precision Engineering Vol. 24(2000), pp.237-244.

[6] W.K. Huang, C.L. Kuo: Study of Magnetic Abrasive Polishing. Chinese Mechanical Engineering Society, Ninety Years Republic of China, p.219.

[7] S. Sakka, Y. Tanaka: Journal of Non-Crystalline Solids Vol. 82 (1986), pp.24-30.

[8] Reisser, W. Mebarek and Denise: U. S. Patent 5, 931, 996. (1999).

[9] L.J. Xu: Digital Magnetic Abrasive Surface Processing Technology in Basic Research (M.S., Zhejiang University, China 2004).

In order to see related information, you need to Login.