Corrosion Behavior of Cu60Zr30Ti10 Amorphous Alloy

Abstract:

Article Preview

The ribbon samples for Cu60Zr30Ti10 (at. %) with a thickness of 50 μm and a width of 13 μm were prepared by melt spinning at the wheel speed of 30 m/s. The glassy structure was confirmed by X-ray diffraction (XRD) using Cu Kα radiation. The corrosion property and corrosion mechanism in 1 M HCl, 1 M NaCl, and 0.5 M H2SO4 solutions were investigated by electrochemical polarization measurement. The corrosion mechanisms are dominated by the pitting corrosion in H2SO4 solution and the pitting and uniform corrosion in HCl and NaCl solutions. In addition, the corrosion resistance in H2SO4 solution is better than that in HCl and NaCl solutions. Cu60Zr30Ti10 glassy alloy in H2SO4 solution is nobler than in HCl and NaCl solutions.

Info:

Periodical:

Advanced Materials Research (Volumes 139-141)

Edited by:

Liangchi Zhang, Chunliang Zhang and Tielin Shi

Pages:

498-501

DOI:

10.4028/www.scientific.net/AMR.139-141.498

Citation:

A. H. Cai et al., "Corrosion Behavior of Cu60Zr30Ti10 Amorphous Alloy", Advanced Materials Research, Vols. 139-141, pp. 498-501, 2010

Online since:

October 2010

Export:

Price:

$35.00

[1] W.H. Wang: Prog. Mater. Sci., Vol. 52 (2007) No. 4, pp.540-596.

[2] W.H. Wang, C. Dong and C.H. Shek: Mater. Sci. Eng. R., Vol. 44 (2004) No. 2-3, pp.45-89.

[3] A. Inoue, W. Zhang, T. Zhang and K. Kurosaka: Acta Mater., Vol. 49 (2001) No. 14, pp.2645-2652.

[4] K. Asami, C. Qin, T. Zhang and A. Inoue: Mater. Sci. Eng. A, Vol. 375-377 (2004) No. 1-2, pp.235-239.

[5] C. Qin, K. Asami, T. Zhang, W. Zhang and A. Inoue: Mater. Trans., Vol. 44 (2003) No. 4, pp.749-753.

[6] F.R. Niessen: Cohesion in Metals (Elsevier Science, Amsterdam 1988).

[7] T. Yamamoto, C. Qin, T. Zhang, K. Asami and A. Inoue: Mater. Trans., Vol. 44 (2003) No. 6, pp.1147-1152.

[8] B. Liu and L. Liu: Mater. Sci. Eng. A, Vol. 415 (2006) No. 1-2, pp.286-290.

[9] M.K. Tam, S.J. Pang and C.H. Shek: J. Non-Cryst. Solids, Vol. 353 (2007) No. 32-40, pp.3596-3599.

[10] D.A. Jonse: Principles and Prevention of Corrosion (Printice-Hall, NJ 1996).

[11] A. Tauseef, N.H. Tariq, J.I. Akhter, B.A. Hasan and M. Mehmood: J. Alloys Compd., Vol. 489 (2010) No. 2, pp.596-599.

In order to see related information, you need to Login.