Study on Ultrasonic Test Defects Causes of Medium Plate

Abstract:

Article Preview

In this paper,Q345E steel as the object of study,analysis of several typical internal defects of UST to explore the reasons for failure caused by UST testing.The results show that: the center segregation of Mn/S is likely to induce center segregation structure of P+B with a whole cleaning micro-cracks,large size spherical oxide of Si/Ca is an important incentive for causing micro-cracks;Billet board defect detection defect likely to cause an important reason;crack at the alloying elements sharply higher than the matrix composition.Billet defects is an important reason to cause steel surface defects;the alloying elements in place nearing the crack sharply higher than the matrix composition.

Info:

Periodical:

Advanced Materials Research (Volumes 194-196)

Edited by:

Jianmin Zeng, Taosen Li, Shaojian Ma, Zhengyi Jiang and Daoguo Yang

Pages:

259-262

DOI:

10.4028/www.scientific.net/AMR.194-196.259

Citation:

Y. L. Chen et al., "Study on Ultrasonic Test Defects Causes of Medium Plate", Advanced Materials Research, Vols. 194-196, pp. 259-262, 2011

Online since:

February 2011

Export:

Price:

$38.00

[1] Kelly J E, Michalek K P. Metallurgical Transaction A. Vol. 10 (1988), pp.2589-2602.

[2] Revie R W. Corrosion, Vol. 49 (1993), p.17223.

[3] Taira. Parkins RN. Corrosion, Vol. 3 (1987), pp.130-132.

[4] Wu-Yang Chu. 《Hydrogen damage and delayed fracture》. Beijing: Metallurgical Industry Press, 1988. in chinese.

[5] Fruehan RJ. 《White and preventiv measures reviewed》. MOS: Magang Technology Center, 2002. 26. in chinese.

[6] ZHOU Yuan hua. Heavy Machinery Science and Technology. Vol. 2 (2003), p.40.

[7] Gladman T. Ironmaking and Steel-making. Vol. 19 (1992). pp.453-457.

[8] B.G. Pound. SRI International, Vol. 10 (1987), pp.260-263.

In order to see related information, you need to Login.