Dislocation Generated by Electron Irradiation

Abstract:

Article Preview

Dislocation loop was generated by electron irradiation in nickel aluminum alloy. It is important to know dislocation characteristics obtained from a high energetic electron irradiation. If b is the Burger vector of a dislocation loop and g is the diffraction vector, dislocation loop will appear larger, smaller or disappear for g.b>0, g.b<0 or g.b=0, respectively. Dislocation loop was determined as follows – first, the appearance of dislocation loops is arranged in observation table. Second, based on type of dislocation loop, Burger vector and diffraction vector, appearance of dislocation loop is arranged in calculation table. Third, based on observation and calculation table, Burger vector and type of dislocation loop is determined. The results show that dislocation loops consist of perfect dislocation loops and Frank dislocation loops. The perfect dislocation loops have Burger vectors of ½[0 ] and ½[ 0] while Frank dislocation loops have Burger vectors of ⅓[1 1], ⅓[11 ], ⅓[ 11], ⅓[111], ⅓[1 1], ⅓[11 ] and ⅓[ 11]. All dislocation loops are interstitial types.

Info:

Periodical:

Advanced Materials Research (Volumes 418-420)

Edited by:

Xianghua Liu, Zhengyi Jiang and Jingtao Han

Pages:

744-747

Citation:

Suryanto, "Dislocation Generated by Electron Irradiation", Advanced Materials Research, Vols. 418-420, pp. 744-747, 2012

Online since:

December 2011

Authors:

Export:

Price:

$41.00

[1] Loretto, M.H., Electron Beam Analysis of Materials, (1988), Chapman & Hall, London.

[2] Briyatmoko, B., Samosir, N. and Suryanto, Fractography dan Metalography Tensile Test Sample of Incoloy 800H with and without irradiation, J. Microscopy and Microanalysis, Vol. 3 (2000) 2, p.18.

[3] Hull, D., dan Bacon, D., Introduction to Dislocations, (1989), International Series on Materials Science and Technology, Volume 37, Pergamon Press, Exeter – England.