The Influence of Ni on the Microstructure of Co-Base ODS Alloys


Article Preview

Co-based ODS alloys strengthened by γ΄ precipitates and nanosized oxides are promising high-temperature structural materials. Single solid solution of Al and W in the matrix can not be achieved after mechanical alloying, resulting in the formation of low volume fraction of γ΄ phase and several kinds of secondary phases. The addition of Ni promotes the precipitation of γ΄ phase and reduces the amount of secondary phases by the enlargement of the solid solution limit of Al and W within the matrix. In comparison with the lower fracture strength and cleavage fracture mode of the alloy without the addition of Ni, Ni-containing Co-base ODS alloys exhibit much higher fracture strength and obvious ductile facture mode.



Advanced Materials Research (Volumes 535-537)

Edited by:

Chunxiang Cui, Yali Li and Zhihao Yuan




L. Zhang et al., "The Influence of Ni on the Microstructure of Co-Base ODS Alloys", Advanced Materials Research, Vols. 535-537, pp. 1011-1014, 2012

Online since:

June 2012




[1] M. Nganbe and M. Heilmaier: Int. J. Plast. Vol. 25 (2009), p.822.

[2] J. Sato, T. Omori, K. Oikawa, I. Ohnuma, R. Karinuma and K. Ishida: Science Vol. 312 (2006), p.90.

[3] K. Takezawa, S. Ukai and S. Hayashi: Adv. Mater. Res. Vol. 239-242 (2011), p.864.

[4] A. Suzuki and T.M. Pollock: Acta Mater. Vol. 56 (2008), p.1288.

[5] Ping D H, Cui C Y, Gu Y F and Harada H: Ultramicroscopy, Vol. 107 (2007), p.791.

[6] Cui C, Ping D and Gu Y: Mater. Trans. Vol. 47 (2006), p. (2099).

[7] L. Zhang, X.H. Qu, X.B. He, R. Din, H.S. Liu, M.L. Qin and H.M. Zhu: J. Mater. Eng. Perform. Doi: 10. 1007/s11665-012-0206-3.

[8] L. Zhang, S. Ukai, T. Hoshino, S. Hayashi and X.H. Qu: Acta Mater. Vol. 57 (2009), p.3671.

[9] L. Zhang, X.H. Qu, X.B. He, R. Din, Mingli Qin and H.M. Zhu: J. Alloys Compd. Vol. 512 (2012), p.39.

[10] K. Shinagawa, T. Omori, J. Sato, K. Oikawa and I. Ohnuma: Mater. Trans. Vol. 49 (2008), p.1474.

[11] Ooshima M, Tanaka K, Okamoto N L, Kishida K and Inui H: J. Alloys Compd. Vol. 508 (2010), p.71.

[12] K. Niitsu, T. Omori, M. Nagasako and K. Oikawa: J. Alloys Compd. Vol. 509 (2011), p.2697.

[13] G. Östberg, B. Jansson and H.O. Andrén: Scripta Mater. Vol. 54 (2006), p.595.

[14] M. Nganbe, M. Heilmaier and L. Schultz: Z. Metallkd. Vol. 96 (2005), p.625.

[15] S. Takaki, K. Kawasaki and Y. Kimura: J. Mater. Proccess. Technol. Vol. 117 (2001), p.359.